Oxygen transport,thermal and electrochemical properties of NdBa0.5Sr0.5Co2O5+δ cathode for SOFCs

In this study, the crystal structure, thermal, oxygen transport, electrical conductivity and electrochemical properties of the perovskite NdBa_0.5Sr_0.5Co₂O_5+δ (NBSC55) are investigated. In the temperature range of 250 °C–350 °C, the weight loss upon heating was due to a partial loss of lattice oxygen and along with a reduction of Co⁴⁺ to Co³⁺. The tend of weight-loss slows down as temperature increased above 350 °C indicating a reduction of Co³⁺ to Co²⁺ during this stage. The oxygen migration is dominated by surface exchange process at high temperature range (650-800 °C); however, the bulk diffusion process prevails at low temperature range (500–600 °C). For long-term testing, the polarization resistance of NBSC55 increases gradually form 3.13 Ω cm² for 2 h to 3.34 Ω cm² for 96 h at 600 °C and an increasing-rate for polarization resistance is around 0.22% h^?1. The power density of the single cell with NBSC55 cathode reached 341 mW cm^?2 at 800 °C.