Microstructure and shear strength evolution of SnAg/Cu surface mount solder joint during aging |
| |
Authors: | Shawkret Ahat Mei Sheng Le Luo |
| |
Affiliation: | (1) DaimlerChrysler SIM Technology Co., Ltd., 200050 Shanghai, China |
| |
Abstract: | The effect of aging at 150°C on the microstructure and shear strength of SnAg/Cu surface mount solder joint has been investigated with comparison to 62Sn36Pb2Ag/Cu. It is found that the diffusion coefficient of intermetallic compounds at SnAg/Cu interface is smaller than that of intermetallic compounds at SnPbAg/Cu interface at 150°. The shear strength of SnAg solder joint is higher and decreases at a smaller rate during aging compared to that of SnPbAg solder joint. The fracture surface analysis shows that as the aging time increases, the fracture takes place along the solder/Cu6Sn5 interface with an extension toward the Sn−Cu intermetallic layer. |
| |
Keywords: | SnAg solder intermetallics surface mount technology (SMT) aging |