碳黑预处理对Pt/C催化剂对甲醇氧化电催化活性的影响

直接甲醇燃料电池(DMFC)由于具有较多的优点而受到广泛的关注. 但是碳载Pt (Pt/C)阳极催化剂电催化活性低是限制其应用的一个主要问题. 为了提高Pt/C催化剂对甲醇氧化的电催化性能, 分别用CO₂, 空气, H₂O₂或HNO₃对常用作为载体的Vulcan XC-72碳黑进行预处理. 结果表明, 在用CO₂, 空气, HNO₃, H₂O₂处理的及未处理的碳黑作载体制得的Pt/C催化剂电极上, 甲醇氧化峰的峰电流密度顺序为39, 33, 32, 20和18 mA•cm^－2, 表明用CO₂处理的碳载体制备的Pt/C催化剂对甲醇氧化有最好的电催化活性和稳定性. 其主要原因是用CO₂处理能减少碳黑表面的含氧基团和增加石墨化程度, 而使碳黑的电阻降低及Pt粒子在碳黑上的分散性变好.

Effect of Pretreatment of Black Carbon on Electrocatalytic Activity of Pt/C Catalyst for Methanol Oxidation

Direct methanol fuel cell (DMFC) has attracted wide attention due to its many advantages. However, its practical application is limited by the low electrocatalytic activity of the anodic Pt/C catalyst usually used for the methanol oxidation. In this paper, in order to increase the electrocatalytic performance of the Pt/C catalyst for the methanol oxidation, the black carbon, usually used as the supporter, was pretreated with CO₂, air, HNO₃ or H₂O₂. The cyclic voltammetric results indicated that the current densities of the anodic peak of methanol oxidation at the Pt/C catalysts with the black carbon pretreated with CO₂, air, HNO₃, H₂O₂ and untreated black carbon were 39, 33, 32, 20 and 18 mA•cm^－2, respectively, illustrating that among the above five kinds of the Pt/C catalysts, the Pt/C catalyst with the black carbon pretreated with CO₂ shows the best electrocatalytic activity and stability for the methanol oxidation. Its main reason is that the CO₂ pretreatment could reduce the content of the oxygen-containing groups on the surface of the black carbon and increase the content of graphite in the black carbon, leading to the low resistance of the black carbon and the increase in the dispersion extent of the Pt particles in the Pt/C catalyst.