Conversion of hydrogen/carbon dioxide into formic acid and methanol over Cu/CuCr2O4 catalyst

Cu/CuCr₂O₄ catalysts were prepared by impregnation method at various calcination temperatures (300, 400, and 500 °C) and then reduced in H₂ stream. The aggregated particles and decreasing surface area/pore volumes of the deactivated catalysts during HCOOH and CH₃OH formations were also observed. Particularly, the EXAFS data showed that first shells of Cu atoms transforms from Cu–O to Cu–Cu after catalytic reactions, their bond distances and coordination numbers are quite different, respectively. It revealed that metallic Cu atoms are one of the important active species over catalyst surface at different reaction temperatures having many unoccupied binding sites for HCOOH and CH₃OH formations. Additionally, the optimal calcination temperature for Cu/CuCr₂O₄ catalysts was demonstrated at 400 °C that attributed to its strongest acidity and basicity. The catalytic reactions in the duration of HCOOH and CH₃OH preparation were proposed that were composed of HCOOH formation, CH₃OH formation, and CH₃OH decomposition happening at CuCr₂O₄, Cu, and CuO active sites, respectively. The highest CO₂ conversion (14.6%), HCOOH selectivity/yield (87.8/12.8%), and TON/TOF values (4.19/0.84) were obtained at 140 °C and 30 bar in 5 h, respectively. Optimal rate constant (2.57 × 10^?2 min^?1) and activation energy (16.24 kJ mol^?1) of HCOOH formation were evaluated by pseudo first-order model and Arrhenius equation, respectively.