Flash sintering of yttria-stabilized zirconia powders coated with nanoscale films of alumina by atomic layer deposition

The addition of small quantities of aluminum oxide (Al₂O₃) to 8 mol% yttria-stabilized zirconia (8YSZ) benefits conventional sintering by acting as a sintering aid and altering grain growth behavior. However, it is uncertain if these benefits observed during conventional sintering extend to flash sintering. In this work, nanoscale films of Al₂O₃ are deposited on 8YSZ powders by particle atomic layer deposition (ALD). The ALD-coated powders were flash sintered using voltage-to-current control and current rate experiments. The sintering behavior, microstructural evolution, and ionic conductivities were characterized. The addition of Al₂O₃ films changed the conductivity of the starting powder, effectively moving the flash onset temperature. The grain size of the samples flashed with current rate experiments was ~65% smaller than that of conventionally sintered samples. Measurement of grain size and estimates of sample density as a function of temperature during flash sintering showed that small quantities of Al₂O₃ can enhance grain growth and sintering of 8YSZ. This suggests that Al₂O₃ dissolves into the 8YSZ grain boundaries during flash sintering to form complexions that enhance the diffusion of species controlling these processes.