Wear behavior and mechanism of single-layer brazed CBN abrasive wheels during creep-feed grinding cast nickel-based superalloy |
| |
Authors: | Wen-Feng Ding Jiu-Hua Xu Zhen-Zhen Chen Hong-Hua Su Yu-Can Fu |
| |
Affiliation: | 1. College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing, 210016, People’s Republic of China
|
| |
Abstract: | Wear behavior and mechanism of single-layer brazed CBN abrasive wheels during creep-feed grinding nickel-based superalloy K424 was investigated. Grinding force and temperature acting on the abrasive wheels were measured. Optical microscopy and scanning electron microscopy were utilized to detect grain protrusion and wheel wear morphology. The normal distribution of the protrusion height of the brazed CBN grains on the wheel surface was determined. The results show that, though the grinding zone temperature is merely about 180°C during creep-feed grinding nickel-based superalloy, the grinding heat still has an important effect on the grain wear owing to the high temperature of the individual grain up to 500–600°C. Wear patterns of brazed wheels are composed of mild wear (attritious wear and grain micro-fracture) and severe wear (grain macro-fracture, erosion of the bonding layer). Strong joining of brazed CBN grains and Ag–Cu–Ti bonding layer improves significantly the resistance to grain pullout. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|