Efficient overall water splitting over a Mo(IV)-doped Co3O4/NC electrocatalyst

To meet the demand of producing hydrogen at low cost, a molybdenum (Mo)-doped cobalt oxide (Co₃O₄) supported on nitrogen (N)-doped carbon (x%Mo–Co₃O₄/NC, where x% represents Mo/Co molar ratio) is developed as an efficient bifunctional electrocatalyst for hydrogen evolution reaction (HER) and oxygen evolution reaction (OER). This defect engineering strategy is realized by a facile urea oxidation method in nitrogen atmosphere. Through X-ray diffraction (XRD) refinement and other detailed characterizations, molybdenum ion (Mo⁴⁺) is found to be doped into Co₃O₄ by substituting cobalt ion (Co²⁺) at tetrahedron site, while N is doped into carbon matrix simultaneously. 4%Mo–Co₃O₄/NC is the optimized sample to show the lowest overpotentials of 91 and 276 mV to deliver 10 mA cm^?2 for HER and OER in 1 M potassium hydroxide solution (KOH), respectively. The overall water splitting cell 4%Mo–Co₃O₄/NC||4%Mo–Co₃O₄/NC displays a voltage of 1.62 V to deliver 10 mA cm^?2 in 1 M KOH. The Mo⁴⁺ dopant modulates the electronic structure of active cobalt ion (Co³⁺) and boosts the water dissociation process during HER, while the increased amount of lattice oxygen and formation of pyridinic nitrogen due to Mo doping benefits the OER activity. Besides, the smaller grain size owing to Mo doping leads to higher electrochemically active surface area (ECSA) on 4%Mo–Co₃O₄/NC, resulting in its superior bifunctional catalytic activity.