Effect of surface roughness on low-cycle fatigue behavior of type 304 stainless steel

The effects of surface roughness on the low-cycle fatigue life of Type 304 stainless steel at 593°C in air have been investigated. It is observed that, at a strain rate of 4 × 10^?3 s^?1 and a total strain range of 1 pct, the fatigue life (N _f cycles) decreases with an increase in surface roughness. Information on crack growthvs strain cycles has been generated, as a function of surface roughness, by the measurement of striation spacing on fractured surfaces of specimens tested to failure. Crack propagation follows the Ina ∞N (wherea is the crack length afterN strain cycles) relation for longer specimen fatigue lives (N_f > 2700 cycles) and departs from Ina ∞N for shorter fatigue lives. A quantitative estimate is made of the number of cycles N_o(r) to generate a crack length equal to 0.1 mm (≈ 1 grain diam). The initial surface roughness significantly affects only the initiation component of specimen life time. The effect of roughness on crack initiation is described byN ₀ (R) = 1012R^?0.21, whereR is the surface roughness (root-mean-square value) in microns.