Effect of modified layered double hydroxide on the flammability of intumescent flame retardant PP nanocomposites

The dodecyl sulfate intercalated CaMgAl-hydrotalcites (layered double hydroxides [LDHs]) were successfully prepared by co-precipitation method, and characterized by X-ray diffraction analysis, infrared spectroscopy (Fourier transform infrared spectra [FT-IR]), thermogravimetry (TG-DTA), scanning electron microscope, and Brunner−Emmet−Teller (BET). The prepared LDHs were added to the intumescent flame retardant (IFR) polypropylene (PP) nanocomposites, and the limiting oxygen index method (LOI), vertical combustion method (UL-94), cone calorimetry (CCT), and other test methods were used to study its thermal stability and combustion performance. The results showed that when the flame retardant was composed of 23 wt% IFR and 2 wt% O-SDS-LDHs, the LOI value of the material was increased to 31.5%, reaching the V-0 level, and the flame retardant performance was significantly improved. The results also showed that there was a significant synergistic effect between IFR and O-SDS-LDHs, which could improve the thermal stability and graphitization degree of PP nanocomposites. In addition, the peak heat release rate, total heat release, and total smoke production of the PP/IFR/O-SDS-LDHs system were 177 kW/m², 101 MJ/m², and 15.4 m², respectively, which were 82.2%, 51.0%, and 23.0% lower than those of pure PP, respectively. These improvements could be attributed to the presence of dense and continuous char layer formed by the synergistic effect.