Electrochemical properties of La1−xSrxFeO3 (x = 0.2, 0.4) as negative electrode of Ni-MH batteries

La_(1−x)Sr_xFeO₃ (x = 0.2,0.4) powders were prepared by a stearic acid combustion method, and their phase structure and electrochemical properties were investigated systematically. X-ray diffraction (XRD) analysis shows that La_(1−x)Sr_xFeO₃ perovskite-type oxides consist of single-phase orthorhombic structure (x = 0.2) and rhombohedral one (x = 0.4), respectively. The electrochemical test shows that the reaction at La_(1−x)Sr_xFeO₃ oxide electrodes are reversible. The discharge capacities of La_(1−x)Sr_xFeO₃ oxide electrodes increase as the temperature rises. With the increase of the temperature from 298 K to 333 K, their initial discharge capacity mounts up from 324.4 mA h g⁻¹ to 543.0 mA h g⁻¹ (when x = 0.2) and from 147.0 mA h g⁻¹ to 501.5 mA h g⁻¹ (when x = 0.4) at the current density of 31.25 mA g⁻¹, respectively. After 20 charge-discharge cycles, they still remain perovskite-type structure. Being similar to the relationship between the discharge capacity and the temperature, the electrochemical kinetic analysis indicates that the exchange current density and proton diffusion coefficient of La_(1−x)Sr_xFeO₃ oxide electrodes increase with the increase of the temperature. Compared with La_0.8Sr_0.2FeO₃, La_0.6Sr_0.4FeO₃ electrode is a more promising candidate for electrochemical hydrogen storage because of its higher cycle capacity at various temperatures.