Microstructure and mechanical properties of Cr3C2 particulate reinforced Al2O3 matrix composites

Al₂O₃ matrix with three grades of Cr₃C₂ particle size (0.5, 1.5 and 7.5 m) composites were fabricated by a hot-pressing technique. Fully dense compacts with Cr₃C₂ content up to 40 vol % can be acquired at 1400 °C under 30 MPa pressure for 1 h. The flexural strength increases from 595 to 785 Mpa for fine Cr₃C₂ particle (0.5 m) reinforced Al₂O₃ matrix composites. The fracture strength is significantly dependent on the fracture modes of matrix (intergranular or transgranular). The transgranular fracture with a compressive residual stress gives a high fracture strength of composites. At the same time, the fracture toughness increases from 5.2 MPa m^1/2 (10 vol % Cr₃C₂) to 8.0 MPa m^1/2 (30 vol % Cr₃C₂) for the coarse Cr₃C₂ particle (7.5 n) reinforced Al₂O₃ matrix composites. The toughening effects of incorporating Cr₃C₂ particles into Al₂O₃ matrix originate from crack bridging and deflection. The electrical conductivity and the possibility of electrical discharge machining of these composites were also investigated.