| 轧辊表面残余应力测试方法的对比试验研究 |
| |
| 引用本文： | 虞付进,华云松,张克华,丁金福.轧辊表面残余应力测试方法的对比试验研究[J].表面技术,2008,37(6):44-46,56. |
| |
| 作者姓名： | 虞付进 华云松 张克华 丁金福 |
| |
| 作者单位： | 浙江师范大学机械装备与测控技术研究所,浙江,金华,321004;上海理工大学,上海,200093;浙江师范大学机械装备与测控技术研究所,浙江,金华,321004;浙江工业大学,浙江,杭州,310032 |
| |
| 基金项目： | 浙江省自然科学基金
|
| |
| 摘 要： | 轧辊体积大且辊面状态又不好,尤其是热轧辊的表面常有氧化膜和微裂纹,在测量时又不能损伤轧辊表面,因此,轧辊残余应力的测量较困难.为验证临界折射纵波法测轧辊表面残余应力的准确性,用超声波法、X射线法和盲孔法对同一试件进行了应力测量.对这3种测量方法所测得的结果进行比较后,评价超声波法的可靠性和有效性.试验结果显示:临界折射纵波法测试的应力值与X射线衍射法和盲孔法测试的结果具有较好的一致性.
|
| 关 键 词： | 残余应力 轧辊 检测方法 临界纵波 |
| 收稿时间： | 2008/8/18 0:00:00 |
| 修稿时间： | 2008/12/10 0:00:00 |
Contrast Experimental Study on Residual Stress Measurement of Roller |
| |
| YU Fu-jin,HUA Yun-song,ZHANG Ke_hua and DING Jin-fu.Contrast Experimental Study on Residual Stress Measurement of Roller[J].Surface Technology,2008,37(6):44-46,56. |
| |
| Authors: | YU Fu-jin HUA Yun-song ZHANG Ke_hua and DING Jin-fu |
| |
| Affiliation: | Institute of Machinery Equipment and Measurement & Control Technology, Zhejiang Normal University, Jinhua 321004, China,University of Shanghai for Science and Technology, Shanghai 200093, China,1. Institute of Machinery Equipment and Measurement & Control Technology, Zhejiang Normal University, Jinhua 321004, China;2. Zhejiang University of Technology, Hangzhou 310032, China and Institute of Machinery Equipment and Measurement & Control Technology, Zhejiang Normal University, Jinhua 321004, China |
| |
| Abstract: | The residual stress measurement of roller is very difficult because that the roller has gigantic volume, the surface is out of order and especially there are oxide film and microcrack. In order to test the veracity of the method of the critical refracted longitudinal wave measurement (CRLWM) , the CRLWM method, the X radial method and the dead hole method were employed to test the residual stress, and the test result of this three methods was compared to evaluate reliability and validity of CRLWM. The result shows that the result of all of the test method is consentaneous. |
| |
| Keywords: | Residual stress Roller Test method Critical refracted longitudinal wave |