Direct synthesis of CeO2/SiO2 mesostructured composite materials via sol–gel process

A series of CeO₂/SiO₂ mesostructured composite materials was synthesized by sol–gel process using Pluronic P123 as template, tetraethylorthosilicate as silica source and hexahydrated cerium nitrate as precursor under acid condition. The as-synthesized materials with Ce/Si molar ratio ranging from 0.03 to 0.3 were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), laser Raman spectroscopy (LRS), and N₂ adsorption. Characterization revealed that all samples possess ordered hexagonal mesoporous structure similar to SBA-15 and possess high surface area, large pore volume and uniform pore size. The fact that cerium species are present as highly dispersed CeO₂ nanocrystals in hexagonal matrix was confirmed by XRD combined with high-resolution TEM and selected area electron diffraction (SAED) analysis. Introduction of ceria to silica matrix can cause a distortion of hexagonal ordering structure and decrease pore diameter and increase the wall thickness of mesopores. Moreover, it can be found that this sol–gel route is a feasible, effective and simple method for templating synthesis of CeO₂/SiO₂ composite materials.