Sodium beta-alumina thin films as gate dielectrics for A1GaN/GaN metal-insulator-semiconductor high-electron-mobility transistors

Sodium beta-alumina（SBA） is deposited on AlGaN/GaN by using a co-deposition process with sodium and Al₂O₃ as the precursors.The X-ray diffraction（XRD） spectrum reveals that the deposited thin film is amorphous.The binding energy and composition of the deposited thin film,obtained from the X-ray photoelectron spectroscopy（XPS） measurement,are consistent with those of SBA.The dielectric constant of the SBA thin film is about 50.Each of the capacitance-voltage characteristics obtained at five different frequencies shows a high-quality interface between SBA and AlGaN.The interface trap density of metal-insulator-semiconductor high-electron-mobility transistor（MISHEMT） is measured to be（3.5～9.5）×10¹⁰ cm^-2·eV^-1 by the conductance method.The fixed charge density of SBA dielectric is on the order of 2.7×10¹² cm^-2.Compared with the AlGaN/GaN metal-semiconductor heterostructure high-electronmobility transistor（MESHEMT）,the AlGaN/GaN MISHEMT usually has a threshold voltage that shifts negatively. However,the threshold voltage of the AlGaN/GaN MISHEMT using SBA as the gate dielectric shifts positively from—5.5 V to—3.5 V.From XPS results,the surface valence-band maximum（VBM-E_F） of AlGaN is found to decrease from 2.56 eV to 2.25 eV after the SBA thin film deposition.The possible reasons why the threshold voltage of AlGaN/GaN MISHEMT with the SBA gate dielectric shifts positively are the influence of SBA on surface valence-band maximum （VBM-E_F）,the reduction of interface traps and the effects of sodium ions,and/or the fixed charges in SBA on the two-dimensional electron gas（2DEG）.