Influences of B2O3/CuO additions on the sintering behavior,microstructure and microwave dielectric properties of 6Nd[(Zn0.7Co0.3)0.5Ti0.5]O3–4(Na0.5Nd0.5)TiO3 ceramics

B₂O₃ and CuO were codoped into 6Nd(Zn_0.7Co_0.3)_0.5Ti_0.5]O₃–4(Na_0.5Nd_0.5)TiO₃ (abbreviated as 6NZCT–4NNT) ceramics as sintering aids. The influences of the sintering aids on the sintering characteristics, microstructure and microwave dielectric properties of the 6NZCT–4NNT ceramics were systematically investigated as a function of the proportion of B₂O₃ and CuO. Codoping could greatly reduce the sintering temperature from 1410 °C to 1150 °C, indicating that B₂O₃/CuO are good sintering aids for 6NZCT–4NNT ceramics. The B₂O₃/CuO sintering aids had no significant impact on the phase purity of the investigated ceramics, even though a solid solution was formed due to Cu²⁺ ion substitution. However, they had evident influences on the surface morphology and grain size. The average grain size was enlarged with increasing amounts of CuO in the B₂O₃/CuO sintering aids. Remarkable deterioration of the microwave dielectric properties for 6NZCT-4NNT ceramics was not observed when codoping an appropriate amount of B₂O₃ and CuO. The 6NZCT–4NNT ceramics codoped with 2.0 mol% B₂O₃ and 2.0 mol% CuO sintered at 1150 °C for 3 h exhibited a homogeneous microstructure and promising microwave dielectric properties: an appropriate dielectric constant (ε_r = 49.37), a high quality factor (QF = 47,295 GHz), and a near-zero temperature coefficient of resonant frequency (TCF = +0.9 ppm/^°C).