Sc3+-doping effects on porous Li3V2(PO4)3/C cathode with superior rate performance and cyclic stability

An enhanced sol-gel combustion method was used to synthesize different porous Sc³⁺-doped Li₃V_2-xSc_x(PO₄)₃/C (x = 0.00, 0.05, 0.10 and 0.15) compounds. The substitution of Sc³⁺ into the V³⁺ sites of Li₃V_2-xSc_x(PO₄)₃/C expands the lattice volume along with the enlargement of Li⁺ diffusion channel, which is beneficial for Li⁺ transportation and ionic conductivity improvement. Besides, the Sc³⁺ doping content exhibits a great impact on the morphology of Li₃V_2-xSc_x(PO₄)₃/C composite. The pristine Li₃V₂(PO₄)₃/C are constituted of porous particles and nanorods, and the ratio of nanorods to particles can be controlled by adjusting the amount of Sc³⁺ doping since the ratio of nanorods to particles decreases with increasing Sc³⁺ doping content. When Sc³⁺ doping content increases to a certain level (x = 0.15, Li₃V_1.85Sc_0.15(PO₄)₃/C), the nanorods are hardly seen. Li₃V_1.90Sc_0.10(PO₄)₃/C with higher tapped density, better reversibility, smaller resistance and larger Li⁺ diffusion coefficient demonstrates outstanding rate performance and cyclic stability, together with high specific discharge capacities of 130.2 and 92.9 mAh g⁻¹ at 0.5 and 20 C, respectively. Furthermore, a superior specific discharge capacity of 85.8 mAh g⁻¹ was retained at 20 C following 1000 cycles. Overall, a novel approach for the preparation of high-performance Li₃V_2-xSc_x(PO₄)₃/C cathodes with different morphologies for lithium-ion batteries is provided.