Patterning Graphene Surfaces with Iron‐Oxide‐Embedded Mesoporous Polypyrrole and Derived N‐Doped Carbon of Tunable Pore Size

This study develops a novel strategy, based on block copolymer self‐assembly in solution, for preparing two‐dimensional (2D) graphene‐based mesoporous nanohybrids with well‐defined large pores of tunable sizes, by employing polystyrene‐block‐poly(ethylene oxide) (PS‐b‐PEO) spherical micelles as the pore‐creating template. The resultant 2D nanohybrids possess a sandwich‐like structure with Fe₂O₃ nanoparticle‐embedded mesoporous polypyrrole (PPy) monolayers grown on both sides of reduced graphene oxide (rGO) nanosheets (denoted as mPPy‐Fe₂O₃@rGO). Serving as supercapacitor electrode materials, the 2D ternary nanohybrids exhibit controllable capacitive performance depending on the pore size, with high capacitance (up to 1006 F/g at 1 A/g), good rate performance (750 F/g at 20 A/g) and excellent cycling stability. Furthermore, the pyrolysis of mPPy‐Fe₂O₃@rGO at 800 °C yields 2D sandwich‐like mesoporous nitrogen‐doped carbon/Fe₃O₄/rGO (mNC‐Fe₃O₄@rGO). The mNC‐Fe₃O₄@rGO nanohybrids with a mean pore size of 12 nm show excellent electrocatalytic activity as an oxygen reduction reaction (ORR) catalyst with a four‐electron transfer nature, a high half‐wave‐potential of +0.84 V and a limiting current density of 5.7 mA/cm², which are well comparable with those of the best commercial Pt/C catalyst. This study takes advantage of block copolymer self‐assembly for the synthesis of 2D multifunctional mesoporous nanohybrids, and helps to understand the control of their structures and electrochemical performance.