Influence of the pre-treatment on the structure and reactivity of Ir/γ-Al2O3 catalysts in the selective reduction of nitric oxide by propene

The selective catalytic reduction (SCR) of nitric oxide by propene over Ir/Al₂O₃ under lean-burn conditions (1000 vpm NO, 2000 vpm C₃H₆, 500 vpm CO, 10 vol.% O₂) was studied. The activity was shown to be strongly enhanced after exposure of the catalyst at 600°C under the reaction mixture, irrespective of the oxidising or reducing pre-treatment. Simultaneously, the Ir dispersion decreased from 78 to 10%. The influence of each component of the reaction mixture on the activation process was examined. The presence of both CO and O₂ was found to be necessary to activate Ir/Al₂O₃ while NO would not be. In situ FT-IR results revealed that initially fully oxidised Ir particles partially reduced in the feed to form Ir⁰ reduced surface sites (νCO at 2060 cm^?1) which adsorbed CO up to 350–400°C. The activation under reactants was related to the formation of these sites. The presence of reduced (or partially reduced) Ir sites, possibly siting at the surface of IrO₂ particles and stabilised by CO adsorption, was proposed to be responsible for the SCR activity.