| Abstract: | Fracture Toughness and Fatigue Crack Growth of Cast Irons Fracture toughness, elastic moduli and fatigue crack growth rates in air and in vacuum were measured for 17 different cast irons. The graphite shape in the cast irons varied from flakes to nodules, the matrix varied from ferrite to pearlite to martensite. In the fatigue crack growth rate tests, using fracture mechanics methods, it was observed that the fatigue crack growth rate increases significantly as the cyclic stress intensity range approaches the critical value for stable crack growth. This phenomenon was used to determine the fracture toughness of the cast irons. Such toughness data agree well with literature data on the fracture toughness of cast irons. An extensive review of the effects of strength on the fracture toughness of commercial cast irons is presented. In cast irons with flake graphite, cyclic loading results in a reduced modulus of elasticity. This is attributed to the rupture of the graphite flakes under cyclic loading. |