Synthesis and characterization of caprolactone based polyurethane with degradable and antifouling performance |
| |
Authors: | Abid Ali Lina Song Jiankun Hu Jingxian Jiang Qingqing Rao Muhammad Shoaib Shah Fahad Yongjie Cai Xiaoli Zhan Fengqiu Chen Qinghua Zhang |
| |
Affiliation: | 1.College of Chemical and Biological Engineering, Zhejiang Provincial Key Laboratory of Advanced Chemical Engineering, Manufacture Technology, Zhejiang University, Hangzhou 310027, China;2.Ningbo Research Institute, Zhejiang University, Ningbo 315100, China |
| |
Abstract: | In this work,a degradable polyurethane composed of caprolactone(CL)and L-Lactide(LLA)as soft seg-ments,and 4,4'-methylenebis(cyclohexyl isocyanate)(H12MDI)and polytetramethylene ether glycol(PTMEG)as hard segments,was prepared.Hydrolytic degradation experiment revealed that the degrad-able polyurethane(PU)could be degraded in artificial seawater.It also showed that caprolactone-co-polyurethane(CL-PU)copolymer with higher crystallinity degraded much slower in artificial seawater.However,the introduction of LLA resulted in an increase in the hydrophilicity and reduction in the crys-tallinity of degradable PU,as demonstrated by the contact angle analysis.The result of the scanning elec-tron microscope showed that the surface of degradable PU renewed under static condition.Moreover,degradable PU was able to be used as a carrier,and it controlled the release rate of 4,5-dichloro-2-octyl-isothiazolone(DCOIT).The anti-diatom(Navicula incerta)test demonstrated that the(caprolactone-co-L-lactide)-co-polyurethane 4(CL/LAx-PU4)with DCOIT contents prevented the adhe-sion of diatom Navicula incerta(88.37%reduction)due to their self-polishing and the release of antifou-lants.Therefore,the degradable PU consisted of CL,LLA,and DCOIT could be a durable resin with good antifouling activity for the application in the marine anti-biofouling field. |
| |
Keywords: | Antifoulant 4 5-dicholoro-2-octyl-isothiazolone Degradable polyurethane L-Lactide Caprolactone |
本文献已被 万方数据 等数据库收录! |
| 点击此处可从《中国化学工程学报》浏览原始摘要信息 |
|
点击此处可从《中国化学工程学报》下载全文 |
|