Structural and lithium intercalation studies of Mn(0.5−x)CaxTi2(PO4)3 phases (0≤x≤0.50)

Materials from the Mn_(0.5?x)Ca_xTi₂(PO₄)₃ (0≤x≤0.50) solid solution were obtained by solid-state reaction in air at 1000 °C. Selected compositions were investigated by powder X-ray diffraction analysis, ³¹P nuclear magnetic resonance (NMR) spectroscopy and electrochemical lithium intercalation. The structure of all samples determined by Rietveld analysis is of the Nasicon type with the R space group. Mn²⁺/Ca²⁺ ions occupy only the M1 sites in the Ti₂(PO₄)₃ framework. The divalent cations are ordered in one of two M1 sites, except for the Mn_0.50Ti₂(PO₄)₃ phase, where a small departure from the ideal order is observed by XRD and ³¹P MAS NMR. The electrochemical behaviour of Mn_0.50Ti₂(PO₄)₃ and Mn_(0.5?x)Ca_xTi₂(PO₄)₃ phases was characterised in Li cells. Two Li ions can be inserted without altering the Ti₂(PO₄)₃ framework. In the 0≤y≤2 range, the OCV curves of Li//Li_yMn_0.50Ti₂(PO₄)₃ cells show two main potential plateaus at 2.90 and 2.50–2.30 V. Comparison between the OCV curves of Li//Li_(1+y)Ti₂(PO₄)₃ and Li//Li_yMn_0.50Ti₂(PO₄)₃ shows that the intercalation occurs first in the unoccupied M1 site of Mn_0.50Ti₂(PO₄)₃ at 2.90 V and then, for compositions y>0.50, at the M2 site (2.50–2.30 V voltage range). The effect of calcium substitution in Mn_0.50Ti₂(PO₄)₃ on the lithium intercalation is also discussed from a structural and kinetic viewpoint. In all systems, the lithium intercalation is associated with a redistribution of the divalent cation over all M1 sites. In the case of Mn_0.50Ti₂(PO₄)₃, the stability of Mn²⁺ either in an octahedral or tetrahedral environment facilitates cationic migration.