Electrical properties of Co-doped CaCu3Ti4O12

Co-doped CaCu₃Ti₄O₁₂ samples were synthesized by solid-phase reaction. Electrical properties were studied by impedance spectroscopy in wide temperature (25–450 °C) and frequency (10 Hz–10 MHz) intervals. It was shown that the presence of the copper oxide interlayer significantly reduces the value of the dielectric constant. The amount of impurity copper in the CaCu₃Ti_4-хCo_хO_12-δ samples (x = 0.06; 0.12; 0.24) rise with an increase in the cobalt content. The samples are characterized by a granular microstructure, with an average grain size ranging from 2 to 10 μm. The impedance of the samples was simulated at a temperature of 25 °C and in the range of 100–450 °C. It was found that the samples are characterized by low- and high-frequency polarization. The conductivity activation energy varied from 0.94 to 0.87 eV depending on the cobalt content. The CaCu₃Ti_3.94Co_0.06O_12-δ sample are characterized by the best values of the dielectric permittivity and the dielectric loss tangent, ε = 400 and tanδ = 0.2 (at 1 MHz and room temperature), respectively.