A New Series of Mo-free 215Cr-35Ni-xW-02N Economical Duplex Stainless Steels |
| |
作者姓名: | Zi-xing ZHANG Qing-xuan RAN Yu-lai XU Xiao-jiang YU Da-wei JIANG Xue-shan XIAO |
| |
作者单位: | Laboratory for Microstructures,Institute of Materials,Shanghai University |
| |
基金项目: | Item Sponsored by National Key Technology Research and Development Program in 12th Five-Year Plan of China(2012BAE04B02);Innovation Fund of Education Commission of Shanghai Municipality of China(12CXY10) |
| |
摘 要: | A new series of economical Mo-free duplex stainless steels 21.5Cr-3.5Ni-xW-0.2N(x=1.8-3.0,mass%) have been developed.The effects of W on mechanical properties and corrosion resistance were investigated,and the microstructures were analyzed by optical microscopy,X-ray diffraction,transmission electron microscopy and electron backscatter diffraction.The designed steels have a balanced ferrite-austenite relation and are free of sigma phase after solution treatment at 750-1 300℃for 30min followed by water-quenching,whereas a small number of Cr23 C6 precipitates were found after solution treatment at 750℃.After solution treatment at 1 050℃,the steel with 1.8%(mass percent)W exhibits the highest room temperature tensile strength due to the strongest work hardening effect, while the steel with 3.0%(mass percent)W exhibits the highest fracture elongation owing to the transformation-induced plasticity(TRIP)effect.The ductile-brittle transition(DBT)and martensite transformation are respectively found in the ferrite and austenite,which deteriorates the impact properties of the steels with the increase of W content.The corrosion resistance of the designed steels is improved with the increase of W content.The pitting resistance of austenite is obviously better than that of ferrite for the designed alloys.Among the designed steels,the steel with 1.8%(mass percent)W is found to be an optimum steel with excellent comprehensive properties and lowest production cost.
|
关 键 词: | 双相不锈钢 经济型 透射电子显微镜 耐腐蚀性能 合金设计 奥氏体相 钼 固溶处理 |
收稿时间: | 2012-07-03 |
本文献已被 CNKI 维普 ScienceDirect 等数据库收录! |
| 点击此处可从《钢铁研究学报(英文版)》浏览原始摘要信息 |
|
点击此处可从《钢铁研究学报(英文版)》下载全文 |