Reduction of Pyrite Cinder Pellets Mixed with Coal Powder |
| |
Authors: | Xiang-dong XING Jian-liang ZHANG Zhen-yang WANG Ke-xin JIAO Xing-le LIU Shan REN |
| |
Affiliation: | 1. College of Metallurgical and Ecological Engineering, University of Science and Technology Beijing,Beijing 100083, China 2. College of Metallurgical Engineering, Xi′an University of Architecture and Technology, Xi′an 710055, Shaanxi, China |
| |
Abstract: | Direct reduction of pyrite cinder in a rotary hearth furnace (RHF) was studied under the condition of laboratory simulation. Effects of reduction temperature, reduction time, molar ratio of carbon to oxygen, and CaO addition on metallization rate as well as compressive strength of the pellets after reduction were discussed. The results showed that the metallization rate and compressive strength were 93.9% and 2160 N per pellet respectively under the conditions of the reduction temperature of 1200 ℃, the reduction time of 16 min, and the molar ratio of carbon to oxygen (xC/xO) of 1.0; adding 2.5% CaO was beneficial to sulfur enrichment in slag phase of pellet, and metallization rate increased slightly while compressive strength decreased. |
| |
Keywords: | pyrite cinder metallization rate compressive strength pellet coal powder    |
本文献已被 CNKI 维普 ScienceDirect 等数据库收录! |
| 点击此处可从《钢铁研究学报(英文版)》浏览原始摘要信息 |
|
点击此处可从《钢铁研究学报(英文版)》下载全文 |
|