WB36钢临界再热粗晶区组织性能
引用本文:王学,常建伟,黄关政,章应霖.WB36钢临界再热粗晶区组织性能[J].焊接学报,2008,29(10):29-32.
作者姓名:王学  常建伟  黄关政  章应霖
作者单位:1. 武汉大学,动力与机械学院,武汉,430072
2. 河南第一火电建设公司,河南,平顶山,467031
基金项目:平顶山市科技攻关计划 
摘    要:用热模拟方法研究了WB36钢(15NiCuMoNb5)临界再热粗晶区(IRCGHAZ)组织特征及性能,分析组织转变过程及M-A组元形成原因,揭示了1RCGHAZ脆化机理。结果表明,IRCGHAZ保持粗大的板条状马氏体组织特征,形成了密集的M-A组元,其中条状M-A组元分布于马氏体板条间,而在原始奥氏体晶界形成链状M-A组元。与一次粗晶区(CGHAZ)、二次粗晶区及过临界再热粗晶区(SCCGHAZ)相比,IRCGHAZ的韧性最低,它将导致接头的局部脆化现象。IRCGHAZ脆化的主要原因是存在于晶内的条状M-A组元,而不是分布于晶界的粒状M-A组元,这是由于条状M-A组元比颗粒状M-A组元更容易引起解理断裂。

关 键 词:低合金高强钢  临界再热粗晶区  组织  脆化  M-A组元
收稿时间:2007/12/10 0:00:00

Study on microstructure and properties of IRCGHAZ in WB36 steel
WANG Xue,CHANG Jianwei,HUANG Guanzheng and ZHANG Yinglin.Study on microstructure and properties of IRCGHAZ in WB36 steel[J].Transactions of The China Welding Institution,2008,29(10):29-32.
Authors:WANG Xue  CHANG Jianwei  HUANG Guanzheng and ZHANG Yinglin
Affiliation:School of Power and Mechanics, Wuhan University, Wuhan 430072, China,Henan No. 1 Power Construction Company, Pingdingshan 467031, Henan, China,Henan No. 1 Power Construction Company, Pingdingshan 467031, Henan, China and School of Power and Mechanics, Wuhan University, Wuhan 430072, China
Abstract:Microstructures and properties in the intercritical reheated coarse-grained heat-affected zone (IRCGHAZ)of WB36 (15-NiCuMoNb5)steel were studied by means of thermal simulation.In particular, the forming of M-A constituent in the IRCGHAZ and its influence on the toughness were investigated.Experimental results show that the coarsing lath martensite (ML)is retained in the IRCGHAZ, however, a great deal of M-A constituents are formed in IRCGHAZ compared with the coarse grain heat-ffected zone (CGHAZ), with elongated M-A constituents distributed at ML boundaries within the prior austenite grain and necklace-like blocky M-A constituents along the prior austenite grain boundaries.The toughness of IRCGHAZ is the lowest compared with that of the CGHAZ, the second CGHAZ and SCCGHAZ, which led to the local brittleness zone in HAZ.The loss in impact value of the IRCGHAZ was due to the formation of elongatedM-A constituents in the interior of the grains, but not related to the formation of necklace-like M-A constituent along the prior austenite grain boundary region.
Keywords:low alloy high strength steel  inter-critically reheated coarse-grained HAZ  microstructure  brittleness  M-A constituent