Fabrication process and electrical behavior of novel pressure-sensitive composites

A novel route was developed to fabricate a new pressure-sensitive composite by dispersing homogeneously conductive carbon particles in an insulating silicone rubber matrix. The composites showed a gradual change in electrical resistivity with applied pressure within percolation threshold region at a constant temperature. This type of gradual fall of resistivity with applied pressure is very important to fabricate pressure sensors. Various amounts of carbon particles were dispersed in a rubber matrix to understand the effect of volume fraction of conductive filler with applying external pressure on resistivity. A quantitative general effective media (GEM) theory was used to understand the resistivity of carbon–rubber composites system over a large range of volume fraction of carbon with applied pressure. The use of two different sizes of silicon rubber particles showed a significant effect in gradual fall of resistivity with applied pressure in the narrow range of percolation threshold. However, a large variation in resistivity from 1st measuring to 10th measuring was observed. A significant improvement in successive measuring of resistivity variation from 1st measuring to 10th measuring was observed when composites were fabricated in hexane solvent media. Finally, nano-sized Al₂O₃ was dispersed to control the resistivity variation upon successive measurement and to improve the mechanical properties of the composites. The material was suggested to use as unique materials as pressure sensors in practical applications mainly for robots.