Ferrite particles coated with biocompatible phases can be used for hyperthermia treatment of cancer. We have synthesized substituted calcium hexaferrite, which is not stable on its own but is stabilized with small substitution of La. Hexaferrite of chemical composition (CaO)_0.75(La₂0₃)_0.20(Fe₂O₃)₆ was prepared using citrate gel method. Hydroxyapatite was prepared by precipitating it from aqueous solution of Ca(NO₃)₂ and (NH₄)₂HPO₄ maintaining pH above 11. Four different methods were used for coating of hydroxyapatite on ferrite particles. SEM with EDX and X-ray diffraction analysis shows clear evidence of coating of hydroxyapatite on ferrite particles. These coated ferrite particles exhibited coercive field up to 2 kOe, which could be made useful for hysteresis heating in hyperthermia. Studies by culturing BHK-21 cells and WBC over the samples show evidence of biocompatibility. SEM micrographs and cell counts give clear indication of cell growth on the surface of the sample. Finally coated ferrite particle was implanted in Kasaulli mouse to test its biocompatibility. The magnetic properties and biocompatibility studies show that these hydroxyapatite coated ferrites could be useful for hyperthermia.     

TEM Studies of High Temperature Corrosion Behaviour of TiAl Intermetallics with Surface Modifications

The oxidation/sulphidation behaviour of a Ti‐46.7Al‐1.9W‐0.5Si alloy with a TiAl₃ diffusion coating was studied in an environment of H₂/H₂S/H₂O at 850^oC. The kinetic results demonstrate that the TiAl₃ coating significantly increased the high temperature corrosion resistance of Ti‐46.7Al‐1.9W‐0.5Si. The SEM, EDX, XRD and TEM analysis reveals that the formation of an Al₂O₃ scale on the surface of the TiAl₃‐coated sample was responsible for the enhancement of the corroison resistance. The Ti‐46.7Al‐1.9W‐0.5Si alloy was also modified by Nb ion implantation. The Nb ion implanted and as received sampels were subjected to cyclic oxidation in an open air at 800^oC. The Nb ion implantation not only increased the oxidation resistance but also substantially improved the adhesion of scale to the substrate.     

化学复合镀层激光处理研究

研究了激光处理对Ni-P -SiC化学复合镀层的影响。借助于扫描电镜、能谱仪、X射线衍射、显微硬度计等设备对激光处理后复合镀层的表面形貌、组织结构及性能进行了综合分析。结果表明 ,对复合镀层进行激光处理可以获得与炉内加热同样的镀层硬度 ,且当激光功率 4 0 0W ,扫描速度 1.5m /min时 ,镀层硬度高于炉内加热的硬度     

T8钢－聚有机硅氧烷仿生减粘降阻复合涂层的特性

研究了Ｔ８钢－聚有机硅氧烷仿生减粘降阻复合涂层的表面润湿性、磨料磨损特性及对土壤的减粘降阻性能与金属材料相比，仿生复合涂层的表面憎水性显著提高，水在其表面上的接触角达９２°；与４５钢相比，其磨料磨损的体积相对耐磨系数为６３％，降阻率达１５．２２％～２２．２７％     

Improving Wear Resistance of the Ni-base Thermal Spray-Welding Coating Using Rare Earths

ＩｍｐｒｏｖｉｎｇＷｅａｒＲｅｓｉｓｔａｎｃｅｏｆｔｈｅＮｉｂａｓｅＴｈｅｒｍａｌＳｐｒａｙＷｅｌｄｉｎｇＣｏａｔｉｎｇＵｓｉｎｇＲａｒｅＥａｒｔｈｓＺｈａｉＧｕａｎｇｊｉｅ（翟光杰）（ＩｎｓｔｉｔｕｔｅｏｆＰｈｙｓｉｃｓ，ＡｃａｄｅｍｉｃａＳｉ...     

埋地管道涂层检测技术现状

文章对各种埋地管道涂层检测技术进行了综述,并指出了各种技术的优缺点及应用前景.     

深孔钻机水刹车传动机构的设计改进

针对深孔钻机水刹车传动机构原设计结构中存在的问题进行分析、研究、并对机构进行了改进，满足了钻机绞车的各项性能指标和技术要求。     

医用聚氯乙烯材料的表面光接枝改性

研究了在不排氧氛围下 ,紫外光照射 ,以二苯甲酮 (BP)为光引发剂 ,甲基丙烯酸缩水甘油酯(GMA)在医用聚氯乙烯 (PVC)薄膜表面的气相接枝聚合。探讨了反应条件对接枝结果的影响 ,并用正交法指出了影响因素的显著性。用傅立叶红外 (FT- IR)、水接触角作为接枝改性结果的表征。FT- IR谱图表明 GMA已接枝到 PVC膜表面。水接触角由接枝前的 78°下降到 5 4°     

Inhibition of acid rock drainage from uranium ore waste using a conventional neutralization and precipitation treatment

Glass columns (length 50 cm, i.d. 4 cm) containing 900 g of uranium ore waste were subjected to a three-step process: (1) acid drainage generation, (2) neutralization and precipitation treatment and, again, (3) acid drainage generation. In the first acid generation step, lasting about one year, different variables (pyrite addition, inoculation and irrigation solution) were tested by measuring effluent pH, redox potential, total iron and sulphate. Conditions of acid generation were satisfactorily reproduced, reaching stable pH values around 2.0 that were determined mainly by pyrite addition and the type of irrigation solution used (distilled water or ferrous sulphate). The neutralization and precipitation treatment consisted of alternating irrigations of a neutralizing solution (CaO saturated plus NaOH) and a precipitating solution (ferric sulphate saturated). This treatment caused accumulation of basic iron sulphate and iron oxide precipitates according to SEM studies. After this treatment, the barrier effect created by the reaction products was checked, using irrigation solutions similar to the first step. The effluents collected showed higher pH and lower redox potential, total iron and sulphate values than those observed before the treatment, evidencing inhibition of acid drainage generation.     

旋风分离器结构改进的研究

根据旋风分离器的工作原理及应用特点 ,分析了影响旋风分离器分离效率的因素及结构存在的问题 ,并提出了改进措施 ,即内管外壁增设螺旋翼片 ,扩散形锥体改为悬挂挡板。通过实验观察 ,改进结构的旋风分离器分离效率比常规旋风分离器高。实践证明 ,对于密度差异较小的非均相物系的分离 ,只要对旋风分离器作适当改进 ,仍能取得令人满意的效果 ,这大大拓宽了旋风分离器的应用领域