Formation of p-type ZnO film on InP substrate by phosphor doping

ZnO thin film was initially deposited on InP substrate by radio frequency (rf) magnetron sputtering and the diffusion process was performed using the closed ampoule technique where Zn₃P₂ was used as the dopant source. To verify the junction formation of ZnO thin films, the electrical properties were measured, and the effects of Zn₃P₂ diffusion on ZnO thin films were investigated. It is observed that the electrical property of the film is changed from n-type to p-type by dopant diffusion effect. Based on the results, it is confirmed that ZnO thin films can be a potential candidate for ultraviolet (UV) optical devices.     

基片温度对坡莫合金薄膜结构和磁电阻的影响

用磁控溅射方法制备了系列坡莫合金Ni80Fe20薄膜。利用X射线衍射、扫描电子显微镜和原子力显徽镜分析了薄膜的结构、晶粒取向、薄膜厚度、截面结构和表面形态。用4点探测技术测量了薄膜的电阻和磁电阻。结果表明：随衬底温度的升高，晶粒明显长大。膜内的缺陷和应力显著减小，而且增强了薄膜晶粒的[111]择优取向。结果表明，薄膜电阻率显著减小，而磁电阻显著增大。     

Structure and mechanical properties of Al/AlN multilayer with different AlN layer thickness

Nanometer scale Al/AlN multilayers have been prepared by dc magnetron sputtering technique with a columnar target. A set of Al/AlN multilayers with the Al layer thickness of 2.9 nm and the AlN layer thickness variation from 1.13 to 6.81 nm were determined. Low angle X-ray diffraction (LAXRD) was used to analyze the layered structure of multilayers. The phase structure of the coatings was investigated with grazing angle XRD (GAXRD). Mechanical properties of these multilayers were thoroughly studied using a nanoindentation and ball-on-disk micro-tribometer. It was found that the multilayer hardness and reduced modulus showed no strong dependence on the AlN layer thickness. Al2.9 nm/AlN1.13 nm multilayer had more excellent tribological properties than single layers and other proportion multilayers with a lowest friction coefficient of 0.15. And the tribological properties of all the multilayers are superior to the AlN single layer.     

p型未掺杂富锌ZnO薄膜的形成和性能研究

以高纯ZnO为靶材,氩气为溅射气体,利用射频磁控溅射技术在石英衬底上生长出纤锌矿结构的富锌ZnO薄膜.薄膜沿(002)择优取向生长,厚约为1.2μm,呈现电绝缘特性.将溅射的ZnO薄膜在10-3Pa,510~1 000 K的温度范围等温退火1 h,室温Hall测量结果表明ZnO薄膜的导电性能经历了由绝缘—n型—p型—n型半导体的变化.XPS测试表明ZnO薄膜的Zn/O离子比随退火温度的升高而降低,但一直是富锌ZnO,说明未掺杂的富锌ZnO也可以形成p型导电.p型未掺杂富锌ZnO薄膜的形成可归因于VZn受主浓度可以克服VO和Zni本征施主的补偿效应.     

基于LiCo0.8M0.2O2 (M=Ni,Zr)薄膜的全固态薄膜锂电池

用射频磁控溅射结合传统退火的方法制备LiCo0.8M0.2O2 (M=Ni,Zr)阴极薄膜．X射线衍射、拉曼光谱、扫描电子显微镜等手段表征了不同掺杂的LiCo0.8M0.2O2薄膜．结果显示,700℃退火的LiCo0.8M0．2O2薄膜具有类似α-NaFeO2的层状结构．通过对不同掺杂锂钴氧阴极的全固态薄膜锂电池Li／LiPON／LiCo0.8M0.2O2的电化学性能研究表明,电化学活性元素Ni的掺杂使全固态电池具有更大的放电容量(56μAh／cm2μm),而非电化学活性元素Zr的掺杂使全固态电池具有更好的循环稳定性．     

Effects of UV photon irradiation on SiOx (0 < x < 2) structural properties

Thin films of a-SiO_x (0 < x < 2) were prepared by reactive r.f. magnetron sputtering from a polycrystalline-silicon target in an Ar/O₂ gas mixture. The oxygen partial pressure in the deposition chamber was varied so as to obtain films with different values of x. The plasma was monitored, during depositions, by optical emission spectroscopy (OES) system. Energy dispersive X-ray (EDX) measurements and infra-red (IR) spectroscopy were used to study the compositional and structural properties of the deposited layers.Structural modifications of SiO_x thin films have been induced by UV photons’ bombardment (wavelength of 248 nm) using a pulsed laser. IR spectroscopy and X-ray photoemission spectroscopy (XPS) were used to investigate the structural changes as a function of x value and incident energy. SiO_x phase separation by spinodal decomposition was revealed. The IR peak position shifted towards high wavenumber values when the laser energy is increased. Values corresponding to the SiO₂ material (only Si⁴⁺) have been found for laser irradiated samples, independently on the original x value. The phase separation process has a threshold energy that is in agreement with theoretical values calculated for the dissociation energy of the investigated material.For high values of the laser energy, crystalline silicon embedded in oxygen-rich silicon oxide was revealed by Raman spectroscopy.     

后退火温度对溅射沉积Pb(Zr0.52Ti0.48)O3铁电薄膜结构和性能的影响

在具有Ti缓冲层的Pt(111)底电极上,用射频溅射工艺在较低的衬底温度(370℃)和纯Ar气氛中沉积Pb(Zr0.52Ti0.48)O3(PZT)薄膜,沉积过程中基片架作15°摇摆以提高膜厚的均匀性。然后将样品在大气中进行5min快速热退火处理,退火温度550-680℃。用XRD、SEM分析薄膜的微结构,RT66A标准铁电测试系统测量样品的铁电和介电性能。结果表明,所沉积的Pt为(111)取向,仅当后退火温度高于580℃,沉积在Pt(111)上的PZT薄膜才能形成钙钛矿结构的铁电相,退火温度在580-600℃时结晶为(110)择优取向,退火温度高于600℃时结晶为(111)择优取向。PZT薄膜的极化强度随退火温度的升高而增加,但退火温度超过650℃时漏电流急剧上升,因此退火处理的温度对PZT薄膜的结构和性能有决定性的影响。     

WS2 超细粉体的固相法合成

WS2 超细粉体的固相法合成;WS2;固相反应;过硫系数;高能球磨;粒度     

Structural and electrochemical studies of annealed LiNiVO4 thin films

We prepared stoichiometric lithium nickel vanadate amorphous thin films by using r.f. magnetron sputtering under controlled oxygen partial pressure. The amorphous films were heated at various temperatures, 300–600 °C, for 8 h. The as‐deposited and annealed thin films were characterized by Rutherford backscattering spectroscopy, nuclear reaction analysis, Auger electron spectroscopy, X‐ray diffraction, scanning electron microscopy and atomic force microscopy. The electrochemical behavior of the various films was studied by the galvanostatic method. The cells were tested in a liquid electrolyte at room temperature, with lithium metal used as the counter and reference electrode. The best electrochemical storage value was obtained with the thin film annealed at 300 °C, which showed superior capacity and small capacity loss during cycling. Copyright © 2007 John Wiley & Sons, Ltd.     

Chloroaqua Complexes [M3S4(H2O)9?xClx](4?x)+ (M = Mo, W; x = 4, 6, 7) and Their Supramolecular Compounds with Cucur[8]uril

Compounds of trigonal cluster chloroaqua complexes with cucurbit[8]uril were synthesized by slowly evaporating HCl solutions of chalcogenides heterometallic cubane cluster complexes of molybdenum and tungsten with cucurbit[8]uril in air; the complexes were characterized by X-ray diffraction analysis: (H₃O)₈[Mo₃S₄(H₂O)_2.5Cl_6.5]₂Cl(PdCl₄)·(C₄₈H₄₈N₃₂O₁₆)· 29H₂O (a = 13.3183(17) Å, b = 13.7104(18) Å, c = 18.225(3) Å; α = 80.263(3)°, β = 77. 958(3)°, γ = 87.149(4)°, V = 3207.4(7) ų, space group P , Z = 1, ρ(calc) = 1.900 g/cm³), (H₃O)₄ [Mo₃S₄(H₂O)₃Cl₆]₂·(C₄₈H₄₈N₃₂O₁₆)₃·68H₂O (a = 21.413(6) Å, c = 49.832(10) Å; γ = 120°, V = 19788(8) ų, space group R , Z = 3, ρ(calc) = 1.695 g/cm³), (H₃O)₆ [Mo₃S₄(H₂O)₃Cl₆]₂Cl₂·(C₄₈H₄₈N₃₂O₁₆)·12H₂O (a = 15.881(2) Å, b = 17.191(2) Å, c = 23.276(4) Å; β = 98.865(15)°, V = 6278.7(15) ų, space group P2₁/c, Z = 2, ρ(calc) = 1.638 g/cm³), [W₃S₄(H₂O)₅Cl₄]₂·(C₄₈H₄₈N₃₂O₁₆)₃·35H₂O (a = 21.038(3) Å; α = 61.20(1)°, V = 6762.0(14) ų, space group R , Z = 1, ρ(calc) = 1.582 g/cm³). The [Mo₃S₄(H₂O)₃Cl₆]²⁻ anion complex was isolated as three geometrical isomers.Original Russian Text Copyright © 2004 by E. V. Chubarova, D. G. Samsonenko, H. G. Platas, F. M. Dolgushin, A. V. Gerasimenko, M. N. Sokolov, Z. A. Starikova, M. Yu. Antipin, and V. P. Fedin__________Translated from Zhurnal Strukturnoi Khimii, Vol. 45, No. 6, pp. 1049–1058, November–December, 2004.