Influence of Polyalkylmethacrylate VII on Boundary Film Formation,Friction,Wear and Efficiency of Lubricants

1 Influence of PAMAon Boundary Fil mFormation and Friction1.1 Experi mental methodsUltra-thin optical interferometry has been used tostudy thinlubricating fil ms for more than a decade and theexperi mental details of this technique have been reportedpreviously[1].The principle of the test setup is shown inFigure1.A polished steel ball is loaded and rolled againstthe flat surface of a glass disc that is coated with a thinsemi-reflecting chromiumlayer and a silica spacer of about500nmthickne…     

Mechanical spectroscopy in commercial Fe–6 wt.% Si alloys between 400 and 1000 K

Mechanical spectroscopy, neutron diffraction and differential scanning calorimetry (DSC) were performed on commercial Fe–6 wt.% Si alloy after quenching from high temperature. The damping spectrum shows a peak at around 800 K and an associated modulus defect. The modulus shows an increase during the second and subsequent heating runs. In addition, an anomaly in the modulus behavior has been found at around 400 K. Different thermal treatments allows to obtain two different recovery degrees of the quenched-in defects. The influence of the recovery degree on the 800 K internal friction peak and on the anelastic modulus has been evaluated and confirm the validity of the grain boundary mechanism associated to this peak. Experimental results are discussed on the basis of recovery and ordering processes.     

MB8镁合金薄板的搅拌摩擦焊

针对我国航空航天工业常用的MB8镁合金。采用搅拌摩擦焊工艺进行焊接，对其焊缝的成形特点、组织特征和力学性能进行分析。结果表明，采用搅拌摩擦焊焊接镁合金效果良好。     

Acoustic emission method for research and control of friction pairs

One of the new physical methods that provides much information about the processes going on in a friction contact zone in real time is acoustic emission (AE). Basic experimental results of AE in friction are presented and analysed. Using AE signals we can get an indication about the state of the friction processes, about the quality of solid and liquid layers on the contacting surfaces in real time, sometimes about intensity of wear, changing of wear and friction regimes and so on. The influence of sliding velocity, load, roughness and some physical and mechanical properties of the body on the parameters of AE are also given. Some attention to the practical implementation of these techniques for control of capability for work of friction pairs in real conditions are given. Modern methods and devices enable condition monitoring of sliding and rolling bearings.     

摩擦焊在钢制实心抽油杆修复中的应用

通过对焊接工艺及焊后热处理工艺优化，采用摩擦焊接技术对报废抽油杆中仍有使用寿命的杆头与杆体进行了拼接，获得了性能达标的抽油杆。从而提高了旧杆的修复率．降低了采油成本。该技术可在抽油杆修复及相关行业进行推广应用。     

磨损自补偿添加剂在成品油中的摩擦学效应

利用四球试验机考察了二聚酸－3－氯－2－羟基丙单酯（DAE）在4种成品油中的摩擦学性能。试验结果表明，DAE添加剂在L－HM68液压油和L－DAB100空压机油中具有良好的适应性，使其承载能力增强，摩擦系数降低及耐磨性增强；DAE在L－CKE涡轮蜗杆油中使耐磨性增强；DAE在L－CKC150齿轮油中虽使承载能力提高，减磨性增强，但有使耐磨性减小的趋势，说明DAE在不同的油中有不同的性能。     

Microstructure and Mechanical Properties of Heat-treated GeSb_2Te_4 Thin Films

The effect of annealing on microstructure,adhesive and frictional properties of GeSb 2 Te 4 films were experimentally studied.The GeSb 2 Te 4 films were prepared by radio frequency(RF)magnetron sputtering,and annealed at 200℃and 340℃under vacuum circumstance,respectively.The adhesion and friction experiments were mainly conducted with a lateral force microscope(LFM)for the GeSb 2 Te 4 thin films before and after annealing.Their morphology and phase structure were analyzed by using atomic force microscopy(AFM)and X-ray Diffraction(XRD)techniques,and the nanoindention was employed to evaluate their hardness values.Moreover,an electric force microscope(EFM)was used to measure the surface potential. It is found that the deposited GeSb 2 Te 4 thin film undergoes an amorphous-to-fcc and fcc-to-hex structure transition;the adhesion has a weaker dependence on the surface roughness,but a certain correlation with the surface potential of GeSb 2 Te 4 thin films.And the friction behavior of GeSb 2 Te 4 thin films follows their adhesion behavior under a lower applied load.However,such a relation is replaced by the mechanical behavior when the load is relatively higher.Moreover,the GeSb 2 Te 4 thin film annealed at 340℃presents a lubricative property.     

聚醚合成工业齿轮油的研制

以聚醚为基础油辅以抗磨剂、抗氧剂、防锈剂等多种添加剂研制而成的KGW聚醚合成工业齿轮油具有优异的黏温性能和低温性能，优异的极压抗磨性，极优的减摩性能，可满足高负荷、强冲击等苛刻条件下各类齿轮传动装置的润滑要求。该系列产品达到国外同类油品质量水平。     

应用摩擦改进剂提高燃料经济性

介绍了摩擦改进剂的类型及作用机理，比较了不同类型的摩擦改进剂。阐述了应用摩擦改进剂减少边界润滑和混合润滑状态下的摩擦损失，从而提高燃料经济性。     

2-巯基苯并噻唑衍生物摩擦学性能的研究

合成了S—(1—(2—苯并噻唑基巯基)—2—羟基)—丙基N，N—二烷基二硫代氨基甲酸酯和S—(1—(2—苯并噻唑基巯基)—2—乙酰基)—丙基N，N—二烷基二硫代氨基甲酸酯两种化合物。运用IR、MS、HNMR和元素分析等分析方法对其结构进行表征。用四球试验、HQ—l环块试验分别考察了其对润滑油的极压承载能力及抗磨减摩性能的影响。结果表明：在350SN中性油中添加所合成的化合物后可以显著降低四球长磨后磨斑直径、有效地降低摩擦副之间的摩擦系数，拥有优良的摩擦学性能。