Verhalten von Magnesiumlegierungen für Anwendungen im Fahrzeugbau bei mechanisch‐elektrochemischer Komplexbeanspruchung: Einfluss passivierender Deckschichten und Mechanismen der lokalen Schädigung

Behavior of Magnesium‐Alloys for Automotive Applications under Mechanical and Environmental Loading: Influence of Passivating Films and Mechanisms of Local Breakdown To assure an efficient design of components under cyclic loading, all available data concerning fatigue have to be observed. Therefore the influences of manufacturing on the material condition, the mechanical loads and environmental effects have to be analysed. Magnesium‐alloys are of special interest for lightweight applications because of their excellent strength‐density ratio. The corrosion resistance of magnesium‐alloys depends on the same factors that are critical to other metals. The alloys have a good stability to atmospheric exposure and a good resistance to attack by alkali, chromic and hydrofluoric acids. However, because of the electrochemical activity of magnesium, the relative importance of some factors is greatly amplified. The nature and composition of passive films formed on magnesium‐alloys depend on the prevailing conditions, viz. alloy‐composition, passivation potential, pH, electrolyte composition and temperature. Passive films may be damaged by local breakdown. Because of this, magnesium‐alloys suffer a degradation of their properties when exposed to an aqueous environment. The main topic of the present investigations is the verification of mechanisms of the local breakdown of the protecting film. At least two mechanisms are possible for this localization: mechanical breakdown by slip steps and electrochemical breakdown (for e.g. by the effects of chloride ions). Corrosion and passivation of different high purity alloys have been studied in different solutions (neutral, alkaline with specific anions and cations) using electrochemical techniques. The diecasted alloys were tested as produced and machined. The results clarified that depending on alloy/material and surface condition/corrosion environment different mechanisms for electrochemical breakdown of the protecting films are possible. Hence fatigue life under environmental loading is influenced by surface and testing conditions.     

6种金属材料在典型工业大气中的腐蚀规律

选取具有代表性的碳钢、不锈钢、镀锌碳钢、铝、钛和铜挂片,在某企业不同部位投放后进行为期半年的大气腐蚀试验,得出了在半年期中的腐蚀规律。在此基础上,对每种金属材料的腐蚀特点进行总结,并对大气腐蚀的各种影响因素进行分析,提出了行之有效的防护措施。     

含硫化氢气井钻井过程中的腐蚀因素与防护研究

在含硫气井的钻井过程中对于HRC大于22的钻具钢材除了腐蚀疲劳之外，在pH值小于9的环境中会发生硫化物应力腐蚀破裂，这种破坏比腐蚀疲劳更突然、更快，使钻杆大量损坏。含硫气井在钻井过程中，由于湿硫化氢的出现，常常会出现油管、套管、钻井设备、钻井仪器以及对支持保护管柱的水泥环柱等腐蚀和损坏问题，为此，阐述了湿硫化氢的腐蚀特点、机理，归纳总结了影响腐蚀的因素，综述了如何在这些方面防止其腐蚀，使损失减小，为指导油管、套管防腐工程实践提供了依据。建议在钻井过程中采用碱性钻井液，其pH值可到9或更高(至pH值12)，以减缓或防止钻井过程中电化学从硫化物应力腐蚀破裂；含硫气井用的钻杆应该间歇使用。钻杆停用堆置时间可使其放氢，使钻杆恢复韧性，防止硫化物应力腐蚀断裂。     

细节决定采输卤的成败

通过认真学习《细节决定成败》，结合井矿盐开采的实际，分别以生产过程中的三个细节为主，讨论了在采输卤生产技术控制中的细节的重要性。     

高抗挤厚壁套管的性能及应用效果评价

中原油田套管损坏的主要原因是现有套管强度不够,无法抵抗盐膏层段的巨大外挤力。开发了TP130TT型高抗挤厚壁套管,其强度能很好地抵抗盐膏层巨大外挤力。实验室试验表明,各项性能指标达到了设计要求,现场使用取得了很好的效果,解决了中原油田盐膏层段套管强度不足的难题。     

Intergranular corrosion of a light aircraft aluminum alloy propeller

Examination of the wreckage of a light aircraft revealed that approximately 20 cm was missing from one tip of the aluminum alloy propeller. Fractographic and metallographic examination of the remaining portion of the propeller revealed extensive grain-boundary separation in the vicinity of the fracture, and grain edges and corners rounded by corrosion on the fracture surface. Energy dispersive X-ray analysis (EDXA) revealed fluorine on, and in the vicinity of, the fracture surface. In the ensuing litigation, it was asserted that the crash occurred because the propeller fractured in flight as the result of intergranular attack caused by the use of a fluorine-bearing cleaner.     

On the corrosion fatigue crack initiation model and expression of metallic notched elements

In the present study, attempts are made to extend the application of the mechanical model for the fatigue crack initiation (FCI) and the FCI life formula of metallic notched elements in laboratory air to those in the corrosive environment. The test results and analysis of the corrosion FCI (CFCI) life of aluminum alloys and Ti---6A1---4V show that the expression of the CFCI life obtained by modifying the FCI life formula in laboratory air can give a good fit to the test results of the CFCI life. The salt water (3.5% NaCl) environment has no effects on the CFCI resistant coefficient compared with the FCI resistant coefficient in laboratory air. However, 3.5% NaCl environment greatly decreases the CFCI threshold of aluminum alloy, but has little effect on the CFCI threshold of Ti---6A1---4V. The loading frequency ranging from 1 Hz to 10 Hz has no appreciable effect on the CFCI life, and thus, the CFCI threshold of aluminum alloys investigated. Hence, the expression for the CFCI life of metallic notched elements proposed in this study is a better one, which reveals a correlation between the CFCI life and the governing parameters, such as, the geometry of the notched elements, the nominal stress range, the stress ratio, the tensile properties and the CFCI threshold. However, this new expression of the CFCI life needs to be verified by more test results.     

核电材料在模拟反应堆环境中应力腐蚀破裂测试技术与性能评价

简要介绍了采用慢应变速率试验，Ｕ型弯曲和Ｃ形环试验等技术，分别对８００合金，３０４和３１６及３１６Ｔｉ不锈钢Ａ５３３Ｂ压力容器用多在模拟核反应堆环境中的应力腐蚀破裂敏感性性进行的试验研究的一些主要结果；并结合电化学测试和表面膜俄歇电子能谱分析结果进行了讨论。     

合成氨中置锅炉的修复

本文在分析中置锅炉失效原因的基础上，提出了详细的修复措施，为类似情况的设备修复提供了借鉴。