Effects of Rare Earths on Toughness of 31Mn2SiRE Wear-Resistance Cast Steel

The toughness of 31Mn2SiRE wear-resistance cast steel were increased by means of RE compound modification and high temperature austenitizing. The results show that the microstructures can be refined, needle and network ferrite are eliminated, the dislocation density and the quantity of dislocated martensite are increased remarkably, and the shape and distribution of inclusions are improved by the addition of RE. Therefore, the mechanical properties of the modified steel can be greatly increased, especially the toughness (αK) by 44%, yield strength (σs) by 10%, and elongation (δ5) by 42%.     

轻质滤料滤池的试验与研究

轻质滤料滤池是以比水密度略小的滤料为滤床的滤池，通过以净水厂的原水和污水处理厂的二级处理出水为过滤试验对象，所取得的结果表明：下向流轻质滤料滤池对浊度和悬浮固体（SS）的去除率分别可以达到80％和45％，而滤床的水头损失不超过15cm。因此轻质滤料滤池可以以预过滤的形式配置在过滤处理的净水和污水的处理工艺中。     

Ring‐opening polymerization of lactones initiated by diphenylzinc–coinitiator systems

Diphenylzinc, alone or in combination with water and butanone as coinitiators, was used as a polymerization initiator system for a variety of lactones at varying temperatures. The resulting data indicate that the course of the polymerization is greatly influenced by the lactone structure, as well as by the molar ratio of coinitiator to diphenylzinc. When used alone, diphenylzinc exhibited high activity as an initiator in δ‐valerolactone polymerizations, although it was less efficient when used in the β‐butyrolactone and the β‐propiolactone polymerizations. Activity in the polymerization of β‐lactones was increased by adding small amounts of butanone or water. It was also observed that the diphenylzinc–butanone combination was more effective than the diphenylzinc–water mixture in the polymerizations of β‐butyrolactone and β‐propiolactone. Copyright © 2003 Society of Chemical Industry     

Recovery of gold cyanide using inherently conducting polymers

Removal of gold from basic solutions containing [Au(CN)₂]^? has been demonstrated using the inherently conducting polymer polypyrrole. Polymers containing sulfonated aromatic dopants have been found to display a significant ability to remove gold from such solutions. Experiments performed in solutions containing both gold and copper cyanide complexes indicate that the recovery process is not highly selective. However, the polypyrroles used display significantly faster rates of gold recovery than activated carbon. © 2003 Society of Chemical Industry     

Mechanical properties of polyethylene mixtures crystallized under high pressure

The mechanical properties of a medium molecular weight polyethylene (MMW‐PE) and an ultrahigh molecular weight PE (UHMW‐PE) binary mixture with different weight fractions crystallized from the melt at 0.1 and 450 MPa were studied. The tensile modulus, yield stress, and strain were obtained as a function of the weight fractions in the PE mixtures at 25 and 85°C. The tensile modulus in the sample crystallized at 0.1 MPa decreased from 1.5 GPa of pure MMW‐PE to about 0.4 GPa of pure UHMW‐PE with the UHMW‐PE content but it did not decrease with the UHMW‐PE in the sample crystallized at 450 MPa in testing at 25°C. A decreasing rate of the storage modulus E′ of UHMW‐PE in a dynamic measurement for the sample crystallized at 0.1 MPa with the temperature is larger than that of the sample crystallized at 450 MPa. These experimental facts are interpreted in relation to the molecular motion and crystallinity of the sample. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 87: 1962–1968, 2003     

化学复合镀层激光处理研究

研究了激光处理对Ni-P -SiC化学复合镀层的影响。借助于扫描电镜、能谱仪、X射线衍射、显微硬度计等设备对激光处理后复合镀层的表面形貌、组织结构及性能进行了综合分析。结果表明 ,对复合镀层进行激光处理可以获得与炉内加热同样的镀层硬度 ,且当激光功率 4 0 0W ,扫描速度 1.5m /min时 ,镀层硬度高于炉内加热的硬度     

机械合金化Fe-Ni粉末的相结构

使用XRD和Moessbauer等方法，研究了在Ar气氛下机械合金化Fe—Ni粉末相结构的变化．结果表明，在机械合金化Fe64-Ni36粉末过程中，fcc相的数量随着球磨时间的增加先增加然后减少，与加乙醇球磨Fe64-Ni36的情形相同．当Ni的含量(原子分数)大于50％时，有fcc相、顺磁相和FeNi3形成，当Ni的含量低于50％时，bcc相的数量随着Ni含量减少而增加．Moessbauer谱的结果表明，因球磨时间或Fe、Ni比例的不同，Fe—Ni球磨粉末固溶体具有不同结构的原子配比。     

Anthocyanin composition of the red wine Babić affected by maceration treatment

Identification of anthocyanins in the wine made of the Croatian autochthonous grape variety of Babić (Vitis vinifera L.) was carried out and their profile was determined by means of high-performance liquid chromatography with diode array and mass spectrometric detection. Dependence of anthocyanins content and profile on maceration treatment conditions was investigated. Statistically significant differences of anthocyanins concentration in wines Babić produced by various maceration treatments were confirmed by the use of multivariate analysis of variances. The investigation results indicated that the maceration temperature exerts higher influence on anthocyanins concentration than the duration of maceration. In addition, on the basis of anthocyanin composition and using different multivariate statistical analyses, differentiation of wines Babić according to maceration treatments was procured.     

洼60-H26水平井套铣打捞技术

洼60-H26井是一口中曲率水平井,设计井深1 922 m,由于地面条件的限制,设计采用三维井眼轨道。该井水平段在钻至井深1 801 m时,发生卡钻事故。在卡钻事故处理过程中,采用测卡、爆炸松扣技术取出上部钻具后,应用了不同规格的套铣管对被卡钻具进行套铣,采用间歇式套铣方式实现了大斜度井段(45°-90°)的安全套铣,采用短套铣管完成了时水平井段内φ215．0 mm稳定器的套铣,采用φ228．6 mm套铣管成功套铣水平井段被卡LWD仪器,最后通过震击器震击成功解卡。详细介绍了洼60-H26水平井卡钻事故的处理过程,分析了在水平段处理卡钻事故的难点。该井处理卡钻事故的经验,对以后水平井施工中处理井下事故、打捞贵重仪器具有借鉴价值。