不同晶相结构ZrO2负载铜基催化剂用于二乙醇胺脱氢反应

通过制备不同晶相结构〔单斜相(m-ZrO_2)、四方相(t-ZrO_2)和无定型(a-ZrO_2)〕ZrO_2载体,再通过沉积沉淀法制得Cu/m-ZrO_2、Cu/t-ZrO_2和Cu/a-ZrO_2催化剂,分别用于催化二乙醇胺脱氢合成亚氨基二乙酸反应。采用XRD、氮气物理吸附脱附、XPS、H_2-TPR、CO_2-TPD对催化剂的结构进行了表征。结果表明,Cu/m-ZrO_2催化剂界面更加有利于Cu~+/Cu~0稳定存在,具有更多的碱性位点,且抗氧化性较好。在二乙醇胺脱氢反应中,Cu/m-ZrO_2催化剂性能最好,反应时间为2.5 h,亚氨基二乙酸收率为97.64%。     

LWIP协议在STLite/OS20操作系统中的移植

介绍了免费的TCP/IP协议栈LWIP开发工具和环境,分析了如何实现LWIP的移植,并给出了一种嵌入式系统与网络互联的新思路。     

基于Internet的远程教育系统模型研究

随着计算机网络技术的发展，远程教学系统的结构发生了重大的变化，逐步由原来的客户机／服务器(C／S)结构转变为基于Internet的浏览器／服务器(B／S)结构。本文提出了基于CORBA技术的B／S结构系统模型。分析了其运行过程，并与传统的结构进行了比较，指明了其优越性。在本文的结尾。指出了使用这种技术的一个具体例子。     

Performance and Commercial Application of the Promoter LCC-A for Maximization of Propylene Yield

1 Introduction Propylene as an important feedstock for organic chemicals is mainly originated from steam cracking and catalytic cracking processes. During the FCC process the propylene content varies with the FCC catalyst and process technology adopted, resulting in significant difference in propylene concentration in the cracked product——LPG. The conventional FCC pro- cess generally gives a propylene yield of around 4%, while the FCC process with maximization of propylene yield can in…     

Cu基络合物催化甲醇液相氧化羰化反应

针对甲醇液相氧化羰基化法合成碳酸二甲酯(DMC)工艺,开发了新型Cu基络合催化剂(CuB rnLm)。对CuB rnLm催化剂的活性及其稳定性进行了研究。实验结果表明,采用该催化剂,甲醇转化率和DMC选择性较高;元素价态和物质结构分析表明,CuB rnLm催化剂循环使用5次后仍保持较好的稳定性。采用正交设计和中心响应曲面法设计实验,并使用S tatistica软件进行统计分析,寻求出反应的主要影响因素,并得到优化的工艺条件:反应温度100~110℃、反应压力3.0~3.5M Pa、反应时间4~6h、CuB rnLm催化剂质量浓度(以甲醇的体积计)0.15~0.20g/mL。在此工艺条件下,甲醇转化率可达23%以上,DMC的选择性为96%~98%。     

浅谈DC/DC变换器控制新方法

文中针对DC/DC变换器的特点,在现有控制和建模方法的基础之上,对DC/DC变换器的现代控制方法进行了归纳和总结,简要讨论了其控制原理,并比较了各种现代控制方法的优缺点,最后对DC/DC变换器控制方法的发展作了一定的展望。     

Use of the Retarded Solution-Reprecipitation Process to Attain a Higher Initial Permeability in MnZn Ferrites

We investigated the effect of various amounts of liquid phase on microstructure development during sintering and the resulting magnetic permeability of MnZn ferrite (MZF) samples. Our results revealed that the microstructure and the final magnetic permeability depend on the thickness of the liquid-phase film during sintering. The solution-reprecipitation (S-R) process, which is associated with an intensive microstructure development in MZF, starts when a continuous liquid-phase film of critical thickness δ_o, which wets the MZF grains, is formed. The solid-state sintering that takes place before the formation of the continuous liquid-phase film is essential for the final microstructure of MZF.     

Mass Transfer in a Flat Gas/Liquid Interface using non‐Newtonian Media

Gas/liquid mass transfer has been investigated using a stirred vessel gas/liquid contactor using non‐Newtonian media and carbon dioxide as absorbent and gas phase, respectively. The volumetric mass transfer coefficients at different operational variables have been determined. Non‐Newtonian media (liquid phase) were prepared as aqueous solutions of sodium carboxymethyl cellulose salt. The influence of the rheological properties, polymer concentration, stirring rate, and gas flow rate on mass transfer was studied for these liquid phases. Kinematic viscosity and density experimental data were used to calculate the average molecular weight corresponding to the polymer employed. The Ostwald model has been used to fit the rheological behavior of aqueous solutions of the polymer employed as absorbent phase. Reasonably good agreement was found between the predictions of the proposed models and the experimental data of mass transfer coefficients.     

Studies on high density polyethylene (HDPE) functionalized by ultraviolet irradiation and its application

The structure and properties of high density polyethylene (HDPE) functionalized by ultraviolet irradiation at different light intensities in air were studied by electron analysis, FTIR spectroscopy, contact angle with water, differential scanning calorimetry and mechanical properties measurement. The results show that oxygen‐containing groups such as C?O, C—O and C(?O)O were introduced onto the molecular chain of HDPE following irradiation, and the rate and efficiency of HDPE functionalization increased with enhancement of irradiation intensity. After irradiation, the melting temperature, contact angle with water and notched impact strength of HDPE decreased, the degree of crystallinity increased, and their variation amplitude increased with irradiation intensity. Compared with HDPE, the yield strength of HDPE irradiated at lower light intensity (32 W m^?2 and 45 W m^?2) increases monotonically with irradiation time, and the yield strength of HDPE irradiated at higher light intensity (78 W m^?2) increases up to 48 h and then decreased with further increase in irradiation time. The irradiated HDPE behaved as a compatibilizer in HDPE/polycarbonate (PC) blends, and the interface bonding between HDPE and PC was ameliorated. After adding 20 wt% HDPE irradiated at 78 W m^?2 irradiation intensity for 24 h to HDPE/PC blends, the tensile yield strength and notched Izod impact strength of the blend were increased from 26.3 MPa and 51 J m^?1 to 30.2 MPa and 158 J m^?1, respectively. Copyright © 2003 Society of Chemical Industry     

EBSP study of the annealing behavior of aluminum deformed by equal channel angular processing

Commercial purity aluminum (99.5%) was fabricated by equal channel angular pressing (ECAP) up to total accumulated strains of approx. 10. The annealing behavior of material deformed to total strains of approx. 1 and 10 was investigated, using heat treatments of 2 h at various temperatures from 100 to 500 °C. The microstructure of the annealed materials was characterized using the electron back-scatter pattern technique. A number of parameters were determined including the distribution and average values of both the boundary spacings and misorientations. For samples deformed to a total strain of 1, annealing resulted in discontinuous recrystallization. For samples deformed to a total strain of 10, annealing resulted in microstructures exhibiting characteristics of both uniform coarsening and, in a number of places, of discontinuous recrystallization. An attempt was made, based on the boundary spacing distributions, to separate these two components. The grain size after annealing was still however small, being just 6.4 μm after 2 h at 300 °C.