Spectral and Laser Properties of Yb:LuAG Transparent Ceramics Fabricated by Tape Casting Method

Yb³⁺‐doped LuAG laser ceramics with different Yb³⁺‐doping concentrations were successfully fabricated by nonaqueous tape casting method and vacuum sintering technology. XRD patterns and SEM morphologies of the ceramics were presented. The optical in‐line transmittance of the Yb‐doped LuAG ceramics was about 83% at 1030 nm. The fluorescence lifetime of annealed and unannealed ceramic samples was compared. From the spectroscopic properties, it can be seen that the ceramics had a large emission cross section of 2.9 × 10^?20 cm² with a FWHM of about 7.2 nm at 1030 nm. Under 100% population inversion, the maximum gain coefficient was estimated to be 12.4 cm^?1 at 1030 nm. With a fiber‐coupled diode laser as pump source, CW laser at 1030 nm was demonstrated and the maximum output power of 338.9 mW was achieved with a slop efficiency of 19%. A tuning range from 1028 to 1036 nm was obtained.     

Ce3+ doped Lu3Al5O12 ceramics prepared by spark plasma sintering technology using micrometre powders: Microstructure,luminescence, and scintillation properties

Ce³⁺ doped Lu₃Al₅O₁₂ (Ce:LuAG) ceramics were fabricated by the solid-state reaction method through spark plasma sintering (SPS) from 1350 °C to 1700 °C for 5 min at a pressure of 50 MPa using micro powders. The average grain size of the SPSed ceramics gradually grew from 0.42 µm (1400 °C) to 1.55 µm (1700 °C), which is nearly one order of magnitude lower than that of vacuum sintered (VSed) Ce:LuAG ceramics (~24.6 µm). Characteristic Ce³⁺ emission peaking at around 510 nm appeared and 92% photoluminescence intensity of room temperature can be reserved at 200 °C revealing excellent thermal stability. The maximum radioluminescence intensity reached around 3 times of VSed Ce:LuAG ceramics and 7.8 times of BGO crystals. The maximum scintillation light yield under γ-ray (¹³⁷Cs) excitation reached 9634 pho/MeV @ 2 μs. It is concluded that SPS technology is a feasible way to develop Ce:LuAG ceramics and further optical enhancement can be expected.     

固相反应法制备 Ce:LuAG透明陶瓷

以Lu（NO3）3和NH4HCO3为原料，采用沉淀法制备了平均粒径约为40nm的Lu2O3粉体，以该粉体和市售的Al2O3、CeO2超细粉体为原料，采用固相反应工艺，经1760℃真空烧结10h，制备出透明的Ce：LuAG陶瓷，该透明陶瓷在可见光范围内的透过率为56％，X射线激发下的发射光谱为Ce^3＋的特征发射，范围在470-650nm，和同类单晶的光谱一致，正好在硅光电二极管的高敏感曲线范围内，满足于闪烁体的性能要求，是一种有应用前景的闪烁材料．     

Scintillation properties of Tm-doped Lu3Al5O12 single crystals

Using the micro-pulling-down (μ-PD) method, Tm-doped Lu₃Al₅O₁₂ (Tm:LuAG) single crystals were grown to examine their scintillation properties. In transmittance spectra, they exhibited about 80% transparency in the wavelengths longer than 320 nm and five absorption lines due to Tm³⁺ 4f–4f transitions were observed. ²⁴¹Am α-ray excited radioluminescence spectra were measured and intense 4f–4f emission peaks were observed with the host emission. When excited by ¹³⁷Cs γ-Ray to obtain pulse height spectra, Tm 1% doped LuAG showed the highest light yield coupled with a photomultiplier (PMT) or a silicon avalanche photodiode (Si-APD). The light yield was estimated to be 5800 and 7300 photons/MeV for PMT and Si-APD, respectively. Decay time profiles consist of two exponential components and the fast and slow components are considered to be attributed to the host and the combination of the host and Tm³⁺ 4f–4f emission, respectively.     

Crystal growth and scintillation properties of Nd-doped Lu3Al5O12 single crystals with different Nd concentrations

Nd 0.1%, 0.5%, 1% and 3% doped Lu₃Al₅O₁₂ (Nd:LuAG) single crystals were grown in the nitrogen atmosphere by the micro-pulling down (μ-PD) method. The grown crystals had a single-phase confirmed by powder XRD analysis. In absorption spectra, some weak absorption lines due to Nd³⁺ 4f-4f transitions were observed and their intensity increased with the increase of Nd concentration. When excited by ²⁴¹Am α-ray, a broad emission peak due to defects in the host lattice at 320 nm and some sharp lines due to Nd³⁺ 4f-4f transitions at wavelength longer than 400 nm were observed. The decay time profiles of Nd:LuAG under γ-ray excitation were well approximated by two exponential function of 340-760 ns and 3-5 μs for each sample. By pulse height measurement using ¹³⁷Cs, Nd 0.5%:LuAG showed the highest light yield of 7600 ± 760 photons/MeV.     

Dual-activator luminescence of LuAG:Mn4+/Tb3+ phosphor for optical thermometry

Mn⁴⁺ and Tb³⁺ singly doped and Mn⁴⁺/Tb³⁺ codoped lutetium aluminum garnet (Lu₃Al₅O₁₂, or simply LuAG) phosphors were synthesized and investigated for the application of optical thermometry. X-ray powder diffraction and luminescence spectroscopy measurements were performed on all samples to analyze their crystal phases and optical properties. In particular, temperature-dependent luminescence of the LuAG:Mn⁴⁺/Tb³⁺ sample was measured at the temperature range of 270–420 K. The results showed that the luminescence intensity of Mn⁴⁺ has gone through a remarkable decline while the luminescence of Tb³⁺ has an only insignificant change with the rise of temperature which leads to a dramatic decrease in the fluorescence intensity ratio (FIR) between the two activator Mn⁴⁺ and Tb³⁺. Further analysis showed that the LuAG:Mn⁴⁺/Tb³⁺ sample used for temperature sensing has a high relative sensitivity with maximum value of 4.3% K⁻¹ at 333 K. Our research indicated that this LuAG:Mn⁴⁺/Tb³⁺ material is a promising candidate for FIR-type optical temperature sensing.     

Mixed precipitants derived nanocrystalline powders and RE doped LuAG transparent ceramics

Lu₃Al₅O₁₂ (LuAG) nanocrystalline powders were synthesized by using ammonium hydroxide (NH₄OH, AH) and ammonium hydrogen carbonate (NH₄HCO₃, AHC) as mixed precipitant. In the absence of sintering aids such as TEOS, MgO or ZrO₂, the obtained LuAG powders showed good sinterability in H₂ atmosphere (PLSH) at low temperature. The in-line transmittance of LuAG ceramic reached 81% in the whole visible light band from 400 nm to 800 nm. The average grain size of obtained transparent ceramics was ranged in 1–6 μm at different sintering temperatures by PLSH. Various kinds of rare earth ions, such as Nd, Yb, Ce, Pr, and Tm doped RE:LuAG transparent ceramics could be prepared by PLSH technology without sintering aids and HIP post-treatment. Through PLSH technology, RE:LuAG transparent ceramics show high optical quality and large aperture size.     

Comparative study of LuxY1-xAG (x=0..1) laser ceramics doped with 5% Yb3+

Materials with high thermo mechanical properties are required as laser media for high-powered lasers. One of such materials is lutetium-aluminum garnet (LuAG) doped with ytterbium. In the present work, we discuss for the first time a full comparative study of 5% Yb-doped LuYAG ceramics with variation Lu/Y ratio. Samples were prepared with addition of B₂O₃, MgO and SiO₂ which were used as sintering aids. Grain sizes, shrinkage curves, lattice constants and transmission spectra were measured for all samples. Thermal conductivity was measured in a wide temperature range for all studied samples. Output power of 12 W and 60% slope efficiency were obtained on the 5% Yb:LuAG disk laser.     

Crystal growth and scintillation properties of Er-doped Lu3Al5O12 single crystals

Er-doped Lu₃Al₅O₁₂ (Er:LuAG) single crystalline scintillators with different Er concentrations of 0.1, 0.5, 1, and 3% were grown by the micro-pulling-down (μ-PD) method. The grown crystals were composed of single-phase material, as demonstrated by powder X-ray diffraction (XRD). The radioluminescence spectra measured under ²⁴¹Am α-ray excitation indicated host emission at approximately 350 nm and Er³⁺ 4f-4f emissions. According to the pulse height spectra recorded under γ-ray irradiation, the 0.5% Er:LuAG exhibited the highest peak channel among the samples. The γ-ray excited decay time profiles were well fitted by the two-component exponential approximation (0.8 μs and 6-10 μs).     

Layered array Al2O3-LuAG: Ce composite ceramic phosphors for high-brightness display

Thermally robust and efficient composite ceramic phosphors (CCPs) combined both the merits of matrix and phosphor have received growing interests. However, high matrix content (e.g., Al₂O₃ >40 wt%) brings diluted activated ion concentration and dropped photoluminescence (PL) quantum yield (QY). Here, a novel layered array Al₂O₃-LuAG: Ce CCP, where Al₂O₃ and LuAG: Ce thin layers (10–250 µm) are alternately arranged, was presented. Owing to the special structure, thermal phonons and photons are respectively routed into Al₂O₃ layers and LuAG: Ce layers, which weakens the influence of Al₂O₃ and heat accumulation on PL properties. Consequently, it exhibits high PLQY (84.1%) and good thermal conductivity (17.1 W·m^?1·K^?1). When it is irradiated under high-power density (27.2 W·mm^?2) blue laser, the luminous efficiency and lumen-density are promoted to 220 lm·W^?1 and 5994 lm·mm^?2, respectively. This work provides a promising new microstructure in developing novel phosphor converters for high-brightness laser phosphor display.