Simultaneous chromizing-aluminizing coating of austenitic stainless steels

Chromium and aluminum were simultaneously co-deposited by diffusion into austenitic stainless steel substrates, by a single-step, pack-cementation process. The mechanism for the formation of diffusion-coated products on 304 and 316 stainless steels and on Incoloy 800 is discussed. The morphologies of the phases formed at the surface, i.e., an external beta layer and an underlying multiphase interdiffusion zone, are presented. The formation of the brittle, , outer layer was minimized by variations in the pack composition and activator. The coated 304 and 316 steels exhibited excellent scaling resistance upon oxidation in air at 1000°C.     

印制板化学镀镍

介绍了采用金属Zn粒子悬浮液活化要镀镍的印制板(PCB)Cu电路表面,使其可以进行化学镀镍的工艺方法,它可以克服Pd-Sn活化的缺点.     

杂多酸催化剂合成漂白活化剂TAED

探讨了以乙二胺、乙酸、和乙酸酐作为原料，采用两步法在杂多酸（HSiW)催化剂作用下制备活性漂白剂四乙酰乙二胺（TAED）的合成工艺条件。得出两步法的最佳条件是：乙二胺：乙酸（物质的量）＝1：2．5，反应温度约120℃，反应时间1．5h；乙二胺：乙酸酐（物质的量）＝1：4，反应温度为140℃，反应时间4h。TAED的产率与杂多酸催化剂性能的好坏有较紧密的关系。     

适用于聚羧酸减水剂的混凝土激发剂研究

提出一种适用于聚羧酸减水剂的复合矿物混凝土激发剂,研究了在不同养护条件、不同掺量下,激发剂对混凝土工作性能及各龄期强度的影响,结合XRD,SEM物相检测探讨了激发剂作用机理,并在连江可门港口泊位工程中试用,测试了掺激发剂混凝土的耐久性能.宏观测试结果表明所研激发剂I型对混凝土工作性能影响不大,能够提高混凝土早期强度,且对后期强度及长期耐久性能无不良影响;微观分析表明激发剂I型的掺入加速了C2S,C3S等矿物的水化,并激发了粉煤灰、矿粉的二次水化反应,混凝土强度发展拐点提前出现.     

硼砂型膏剂渗硼剂的研制

使用硼砂作为渗硼膏剂的供硼剂，对7种活化剂的活化效果进行了研究，发现活化剂的类型和自身熔点的高低对活化效果有影响，氟化物活化效果好于氯化物，熔点高的活化剂活化效果较好，几种活化剂配合使用渗速明显高于单独使用一种活化剂的渗速，利用正交试验法，确定了CaF2,MgCl2和Na3AlF6三种活化剂的最佳配比，所研制的MSG膏剂渗速快，渗层质量好，对碳钢和低合金钢均有良好的渗硼能力。     

AN EFFICIENT ACTIVATIOR ON FLOTATION OF FINE ANTIMONY OXIDE

Recoveryoffineantimonyoxidewithfrothflotationisoneofthemostdifficultproblems.Theoxidemineralisnotonlytobeslimedeasily,butalsotendstoformcolloidinwatersolution,andtoitshydrolysis,onitssurface,thereexistsSbO,inalkalinesolutionandSbO inacidicsolution.UPtonow,traditionalgravityconcentrationmethodhasbeenuniversallyusedtorecoverantimonyoxide.Nowsomeantimonymillsstilluseshakingtabletechnique,buttherecoveryisonlyabout20%.Inflotationsystem,thecolloidofantimonyoxideiseasilyadheredonthesurfaceofsilicif…     

云南某金矿选矿试验研究

针对云南某金矿石金以细粒、微细粒赋存于石英、黄铁矿的性质,在磨矿细度-74μm75%、T31为活化剂、丁基黄药与A25为捕收剂的条件下,采用一粗一扫两精的工艺流程,获得了金精矿品位79.30g/t,回收率89.45%的较好指标。     

复合激发剂对铜炉渣活性影响及充填材料制备

为了实现铜炉渣的废物利用,以碱激发方式为主研究铜炉渣制备矿用胶凝材料的可能性.选取生石灰、NaOH和早强剂组成的混合物作为复合激发剂,开展铜炉渣活性激发和充填材料制备试验,并采用X射线衍射和扫描电子显微镜对铜炉渣水化产物进行分析.试验结果表明,各激发剂对铜炉渣活性的影响顺序依次为生石灰 > 早强剂 > NaOH,在复合激发剂的作用下炉渣净浆试样的7和28 d强度分别可以达到1.5和3.0 MPa以上.铜炉渣尾砂充填料28 d强度为1.0 MPa,流动性良好,满足充填材料要求.铜炉渣早期水化产物主要有片状的Ca(OH)₂和C-S-H凝胶,随着养护时间的增加,C-S-H凝胶Ca/Si比不断减小,水化产物结构更加致密.养护时间至28 d时,铜炉渣中活性成分基本反应完全.     

高惨量粉煤灰混凝土水化进程的试验研究

高掺量粉煤灰混凝土早期二次水化较为缓慢,随后二次速度逐渐加快,激发剂能显著提高粉煤灰的活性,加速高掺量粉煤灰二次水化反应。通过掺加激发剂、减水剂和控制水胶比,高掺量粉煤灰混凝土是可以满足工程需要的。     

浓硫酸催化合成四乙酰乙二胺的研究

采用二步法制备漂白活化剂四乙酰乙二胺TAED，即由乙二胺与乙酸反应生成二乙酰乙二胺DAED，进一步与乙酸酐反应生成TAED。讨论了原料量比、反应温度、反应时间等影响转化率的因素，通过正交试验确定了最佳反应条件：浓硫酸催化下n(乙二胺）:n（乙酸）:n（乙酸酐）=1:2.5:4,150℃反应11～12h，转化率可达68%～70%。