以Ti, 陶瓷粉末和镍基自熔合金粉末按一定比例配置的混合粉末作为预置合金涂层,采用CO2气体激光进行多层熔覆,在Ti600合金表面制备出摩擦磨损性能沿厚度方向呈梯度变化的钛基功能梯度材料(FGM)。利用扫描电镜(SEM)及X射线能谱仪(EDX)分析了材料的微观组织和成份。结果表明,采用合适的合金粉末成份和激光熔覆工艺参数,可以获得原位自生TiC增强颗粒弥散分布且其含量呈梯度变化的钛基功能梯度材料。熔覆层组织均匀细密,各熔覆层之间无明显界限,且与基体呈良好冶金结合。 相似文献
3.
Laser cladding experiment of Ti + Al + SiO2 + C was carried out on Ti6Al4V alloy substrate, thenthe microstructure of the clad layer was analyzed with SEM and its Anti - oxidation function was discussed.Analyses microstructure show that the clad coating can be divided into three zones along the depth direction:clad, binding and heat - affected zones. Ti5Si3 in the clad zone exists in the form of fine dendrites, TiAl matrix filling among Ti5Si3 dendrites plays a role of connecting the Ti5Si3 with the TiAl3 and transferring load,so the clad coating has been strengthened obviously. 相似文献
4.
5.
为改进钛合金(Ti6Al4V)的耐磨性能,应用脉冲Nd:YAG激光进行了钛合金表面熔覆(Ti+Al/Ni)+(Cr2O3+CeO2)复合涂层实验,分析了工艺参数对熔覆层高度、熔深、稀释率的影响,观测了熔覆层的组织与性能。结果表明,熔覆层高度和熔深随单脉冲能量的增加而增大。单脉冲能量20 J,脉宽8 ms,频率5 Hz,扫描速度1.1 mm/s时稀释率达到最小,其值为3.95%。熔覆层组织是在细小树枝晶和共晶基体上散布的未熔Cr2O3颗粒和白亮球状液析Cr2O3,并有硬化TiAl陶瓷颗粒增强相存在。显微硬度明显提高,最高可达1150 Hv,平均是基材的3~4倍。熔覆层和基材实现良好冶金结合,白亮熔合区宽度10~20 μm。通过优化工艺参数,获得连续、均匀、无裂纹和气孔的高质量涂层。 相似文献
1