测量了Cr^4+,YAG、Cr^4+,Mg2SiO4晶体在室温和液氮温度下的荧光光谱,吸收光谱和激发态寿命,讨论了温度变化时,两种晶体中Cr^4+近红外辐射积分强度变化与激光发态寿命变化的关系,得出结论:在77K ̄300K范围内,Cr^4+的^3T2能级荧光辐射截面本身受温度影响不大,Cr^4+辐射荧光的变化,主要是由无辐射弛豫速率随温度变化而引起的。 相似文献
2.
闪光灯泵浦的Nd:KGd(WO4)2激光器 总被引:1,自引:0,他引:1
报道了用闪光灯泵浦的掺钕的钨酸钆镓(Nd3+:KGd(WO4)2激光器.在重复频率1Hz,脉宽120μs的灯泵下,测量了不同透过率下激光输出能量,获得最大输出能量384mJ,斜率效率1.0%,外推阈值0.54J.在调Q运行时,Nd:KGW晶体的斜率效率为0.16%,最大输出能量46mJ. 相似文献
3.
The absorption spectra, fluorescence spectra, and lifetimes of as-grown and annealed Cr,Yb:YAG crystal grown by Czochralski technique have been measured. The broad absorption bands in the visible region increase in intensity and shift to long wavelength after annealing, and the additional absorption around 482 nm may be possibly due to new octahedral Cr4+ center in the crystal, and the increase in the infrared (IR) region is due to the increase of Cra+. The increase of Cr4+ also results in the groud state absorption and the concentration quenching of Ybs+ in Cr,Yb:YAG crystal after annealing, the fluorescence intensity is reduced to 75% and the emission lifetime is shortened from 1.40 to 0.44 ms. 相似文献
4.
5.
A continuous-wave laser oscillation was demonstrated with a Yb-doped fluorapatite (FAP) crystal pumped with a 905 nm Ti:sapphire laser. The output characteristics for different output couplers were investigated. A maximum power of 67mW at a 1043nm wavelength was obtained with 10% output coupler, pumped by a Ti:sapphire laser with 910mW power. This corresponds to a slope efficiency of 26.5%. 相似文献
6.
We report on the spectral properties of Cr,Yb:YAG crystal co-doped with 0.025 at.% Cr and 10 at.% Yb are reported.Using a continuous wave Ti:sapphire laser as a pumping source,we have demonstrated the self-Q-switched Cr,Yb:YAG laser at room temperature.We obtained an average output power as much as 75mW at 1.03μm with a pulse width (FWHM)as short as 0.4μs.The laser experiment demonstrated that the Cr,Yb:YAG crystal exactly combines the Cr^4 saturable absorber and Yb^3 gain medium.The Cr,Yb:YAG crystal can be a most promising self-Q-switched laser crystal for compact and efficient solid-state lasers. 相似文献
7.
8.
9.
10.
掺镱类激光晶体由于具有大的受激发射截面和长的上能级寿命 ,近年来被人们普遍看好为未来激光惯性约束核聚变研究所需要的首选激光材料。掺镱的氟磷酸钙 [Yb:Ca5( PO4) 3F,简称 Yb:FAP]晶体的发射截面为 5 .9× 1 0 - 2 0 cm2 ,上能级寿命为 1 .0 8ms,因此特别适合作高能量激光增益介质。最近我们采用中国科学院上海光学精密机械研究所新生长的高质量Yb:FAP晶体 ,首次在国内实现了连续激光输出。实验中采用的晶体尺寸为 5 mm× 5 mm×1 0 mm,Yb离子的实际掺杂的原子数分数为 1 .3%。考虑到 Yb:FAP晶体的吸收特性和发射特性 ,我们在… 相似文献