Erbium-doped glass showing the wider 1.5-um emission band is reported in a novel oxide system TeO2-WO3-Nb2O5 and their thermal stability and optical properties such as absorption, emission spectra, cross-sections and fluorescence lifetime were investigated. Compared with other glass hosts, the gain bandwidth properties of Er3+ in TWN glass is close to that of bismuth glasses, and larger than those of tellurite, germanate, silicate and phosphate glasses. The broad and flat 4I13/2-4I15/2 emission and the large stimulated emission cross-section of Er3+ ions around 1.5um can be used as host material for potential broadband optical amplifier in the wavelength-division-multiplexing (WDM) network system. 相似文献
2.
Comparative study of spectroscopic properties of Er^3+/Yb^3+-codoped tellurite glass and fibres under 980nm excitation* 下载免费PDF全文
A tellurite fibre of TeO_{2}-ZnO-La_{2}O_{3}-Li_{2}O glass codoped with 20000 ppm ytterbium and 5000 ppm erbium was fabricated by the suction casting and rod-in-tube technologies. The absorption spectrum of Er^{3+}/Yb^{3+} -codoped bulk glass has been measured. From the Judd-Ofelt intensity parameters, the spontaneous emission probability and radiative lifetime τ_{rad} of Er^{3+}:{}^{4}I_{13/2}→{}^{4}I_{15/2} transition for the bulk glass have been calculated. The emission fluorescence spectra and lifetimes around 1.5μm, and subsequent upconversion fluorescence in the range of 500-700nm were measured in fibres and compared with those in bulk glass. The changes in amplified spontaneous emission with fibre length and pumping power was also measured. It was found that the emission spectrum from erbium in fibres is almost twice as broad as the corresponding spectrum in bulk glass when pumped at 980nm. 相似文献
3.
4.
Intense Green Upconversion Luminescence in Er^3+:Yb^3+ Codoped Fluorophosphate Glass Ceramic Containing SrTe5O11 Nanocrystals 下载免费PDF全文
Er^3+ :Yb^3+ codoped tellurite-fluorophosphate (TFP) glass ceramic exhibits much stronger upconversion luminescence. The intensity of the 540nm green light and 651 nm red light of the TFP glass ceramic is 120 times and 44 times stronger than that of the fluorophospahte (FP) glass, respectively. XRD analysis shows that the nanocrystal in TFP glass ceramic is SrTe5O11. TFP glass ceramic also displays much higher upconversion fluorescence lifetime and crystallization stability. The narrow and strong peak at 540nm is very ideal for practical upconversion luminescence realization. This work is a new trial for exploring non-PbF2 involved nanocrystal upconversion glass ceramics. 相似文献
5.
研究了重金属氧氟硅铋酸盐玻璃 (50-x)SiO2 xBi2O3 50PbF2(x=0, 3, 5, 8, 10, 13, 15 mol%)中Er3+离子的吸收光谱、荧光光谱、荧光半高宽、荧光 寿命和热稳定性能.应用Judd Ofelt理论计算了玻璃的强度参数Ωt(t=2,4,6),应用 McCumber计算了能级4I13/2→4I15/2跃迁的受激发射截面. 结果发现荧光半高宽与Ω6有较大联系,Ω6越大,荧光半高宽越宽.对Er3+
关键词:
重金属氧氟硅铋酸盐玻璃
光谱性质
Er3+离子
Judd Ofelt参数 相似文献
6.
Nd~(3+)-doped tellurite glass and a single mode tellurite glass fiber with a core diameter of 8 μm were prepared in this work. The 1.33-μm emission from the ~4F_(3/2)→~4I_(13/2) transition of Nd~(3+) with a spectral bandwidth of 55 nm in tellurite glass fiber is observed. The lifetime of 164 μs of ~4F_(3/2) level and quantum efficiency of about 100% are obtained. 相似文献
7.
Host dependent thermal stability and frequency upconversion of Er^3+-doped heavy metal oxyfluoride germanate glasses 下载免费PDF全文
The upconversion properties of Er^3+-doped heavy metal oxyfluoride germanate glasses under 975 nm excitation have been investigated. The intense green (551 and 529 nm) and relatively weak red (657 nm) emissions corresponding to the transitions ^4S3/2→^4I15/2, ^2H11/2→^4 I15/2 and ^4F9/2 →^4I15/2, respectively, were simultaneously observed at room temperature. The content of PbF2 has an important influence on the upconversion luminescence emission. With increasing content of PbF2, the intensities of green (529 nm) and red (657 nm) emissions increase slightly, while the green emission (551 nm) increases markedly. These results suggest that PbF2 has an influence on the green (551 nm) emission more than on the green (529 nm) and red (657 nm) emissions. 相似文献
8.
9.
Spectral characteristics of the amplified spontaneous emission(ASE)from a novel single mode Er3+ doped tellurite fiber with D-type cladding is reported in this letter.When pumped at 980 nm,an ASE source that has nearly a 100-nm flat FWHM bandwidth is obtained with a fiber length of 30-60 cm. Variation of ASE spectra with pump powers and fiber lengths are measured.Output power up to 2.0 mW is obtained with a launched pump power of 660 mW. 相似文献
10.
通过传统的熔融淬火技术以及后续热处理法制备了Tm3+/Yb3+共掺含LaF3纳米晶锗酸盐微晶玻璃。通过DTA和XRD研究其热性质和LaF3纳米晶的可控析出。通过透过光谱和上转换发光光谱研究了玻璃的光学性能。利用荧光强度比(FIR)技术研究了微晶玻璃样品在980 nm激光激发下的上转换发光光谱与温度的依赖关系。研究发现,该微晶玻璃样品在313~573 K温度范围内的最大绝对灵敏度Sa和最大相对灵敏度Sr分别为2.6×10-4K-1(573 K)和2.3×10-2K-1(313 K)。结果表明,Tm3+/Yb3+共掺含LaF3纳米晶锗酸盐微晶玻璃在温度传感领域具有潜在的应用前景。 相似文献