Random copolymerization of macromonomers as a versatile strategy to synthesize mixed-graft block copolymers

The random copolymerization of norbornene-functionalized macromonomers was explored as a method of synthesizing mixed-graft block copolymers (mGBCPs). The copolymerization kinetics of a model system of polystyrene (PS) and poly(lactic acid) (PLA) macromonomers was first analyzed, revealing a gradient composition of side chains along the mGBCP backbone. The phase separation behavior of mGBCPs with PS and PLA side chains of various backbone lengths and side chain molar ratios was investigated, and increasing the backbone length was found to stabilize the phase-separated nanostructures. The graft architecture was also demonstrated to improve the processability of the mGBCP, compared to a linear counterpart. Investigations of mGBCPs comprised of polydimethylsiloxane and poly(ethylene oxide) side chains exemplified the diverse self-assembled morphologies, including a Frank-Kasper A15 phase, that can be obtained with mGBCPs synthesized by random copolymerization of macromonomers. Lastly, a ternary mGBCP was synthesized by the copolymerization of three macromonomers.     

Molecular dynamics simulation of P-V-T relationship of ZnO with rock-salt structure using pair-wise interactions

Molecular dynamics (MD) method is used to investigate the behavior of the pressure-volume-temperature (P-V-T) relationship, lattice constant and thermal expansivity for ZnO with rock-salt structure at high pressures and temperatures. The interionic potential is taken to be the sum of pair-wise additive Coulomb, van der Waals attraction, and repulsive interactions. The isothermal and isobaric properties are discussed from the corresponding P-V-T relationship, and it is shown that the MD simulation is successful in reproducing the measured volumes of ZnO over a wide range of temperature and pressure. Meanwhile, the equations of state parameters including lattice constant, linear thermal expansion coefficient, and isothermal bulk modulus are calculated and compared with the available experimental data and the latest theoretical results. At an extended pressure and temperature range, P-V-T relationship, lattice constant, and linear thermal expansion coefficient have been predicted. The structural and thermodynamic properties of ZnO with rock-salt structure are summarized in the pressure 0-100 GPa ranges and the temperature up to 3100 K.     

Widely tunable long-period fiber grating with nm-thick higher refractive index film overlay

By introducing a four-layer step-index waveguide modeling, the characteristics of long-period fiber grating (LPFG) with an nm-thick film overlay, which has higher refractive index than that of fiber cladding are investigated in detail. The influence of both the overlay thickness and refractive index on the tuning ability of LPFG is analyzed. The numerical results demonstrate that spectral response of LPFG is divided into three distinct regions as the overlay deposition increases and the shift of resonant wavelength is drastic in some special thickness range. In conjunction with higher-order cladding mode coupling and fiber cladding etching, the sensitivity of LPFG to the overlay refractive index is enhanced significantly and over 120 nm resonant wavelength tunable range is achieved.     

小间隙高放大多丝室及其放电机制

对以强猝灭气体工作的小间隙多丝室及其放电机制进行了研究,实验表明,因为工作在饱和模式区,这种室同时具有很高的气体放大和相当快的时间特性.文中探讨了放电机制,雪崩中空间电荷效应以及电离光子的产生和作用是重要的因素,而其中后一因素又受到强猝灭气体的抑制.     

氮化硼固相转变的船形模型

 船形转变模型是有rBN结构向wBN结构的固相转变模型。在静高压下，相比于以椅形方式，rBN更容易以船形方式转变。     

碳酸氢铵沉淀法制备氧化钇粉体时反应条件对产物粒度的影响

研究了碳酸氢铵沉淀法的反应条件对氧化钇粒度的影响,探讨了粒度变化规律。发现在沉淀反应中,晶型碳酸钇铵的形成与否是影响氧化钇粒度的关键因素。在较低的反应温度下,当碳酸氢铵和氯化钇的浓度大于0.25mol·L-1,摩尔比大于5,陈化时间大于60min时得到碳酸钇铵沉淀,经煅烧可获得粒度(D50)大于1μm的氧化钇。当反应物浓度较低、摩尔比小,陈化时间较短时得到无定型碳酸钇沉淀,煅烧沉淀可获得粒度(D50)小于0.5μm的氧化钇。实验证明选择适当的沉淀反应条件,可制备D50在0.3～10μm范围内的不同粒度级别的氧化钇粉体。     

手性铜催化剂的制备及在环丙烷羧酯酯不对称合成中的应用

３类手性配体ｄ－１０－樟脑磺酸及其衍生物，α－（－）－羟蒎酮及其衍生物，又恶唑啉６衍生物分别与铜（Ⅱ）形成手性铜配合物，催化重氮乙酸酯与１，１－二苯乙烯或异丁烯的环丙烷化加成反应，得到光学活性环丙羧酸酯，不对称诱导最高可达９５％ｅ．ｅ．。     

Patterned langmuir-blodgett films of monodisperse nanoparticles of iron oxide using soft lithography

Langmuir-Blodgett (LB) films of monodisperse iron oxide nanoparticles have been successfully deposited onto patterned poly(dimethylsiloxane) surfaces. These patterned LB films of iron oxide nanoparticles were transferred onto solid substrates using micro contact printing.     

巡游电子系化合物La0.8Ce0.2(Fe1-xCox)11.4Si1.6的磁热效应

对制备的化合物La0.8Ce0.2(Fe1-xCox)11.4Si1.6(x=0.02,0.04,0.06)的相组成、巡游电子变磁转变(IEMT)特性和磁热效应(MCE)进行了研究。粉末X射线衍射结果表明,经1373 K真空退火处理7 d后,化合物La0.8Ce0.2(Fe1-xCox)11.4Si1.6(x=0.02,0.04,0.06)均为单相立方NaZn13型晶体结构。随着Co含量由x=0.02增加到x=0.06,样品的居里温度TC由207 K上升到277 K。在0~1.5 T磁场变化下,x=0.02,0.04,0.06时样品的最大磁熵变|ΔSM(T)|分别为40.17,12.60和7.65 J.kg-1.K-1,可见该化合物有巨大的磁熵变,而且随Co含量的增加最大磁熵变迅速减小。该化合物的巨大磁熵变来源于TC处的一级相变,以及在TC以上由磁场诱导IEMT,但由于Co原子对Fe原子的替代能够抑制变磁转变的发生,因此该系化合物最大磁熵变随Co含量的增加迅速减小。