还原扩散法制备Sm2Fe17Nx磁粉的研究 总被引:3,自引:0,他引:3
研究了还原扩散法制备Sm2Fe17Nx磁粉过程中,还原扩散反应温度和时间对Sm2Fe17合金单相性的影响,以及Sm2Fe17合金渗氮过程中渗氮温度和时间对Sm2Fe17Nx磁粉性能的影响.结果表明当还原扩散反应温度为1423K、反应时间为5小时能得到均相单一的Sm2Fe17合金;在728K温度下渗氮3.5小时后,400目~500目的Sm2Fe17Nx磁粉的各项磁性能达最大值Br=0.8943T,Hc=325.8kA/m,Hcj=420.3kA/m,(BH)max=78.6kJ/m3. 相似文献
3.
The crystal structure of silicate oxyapatite Ca2Y8Si6O26 was indexed as hexagonal,space group P63/m,a=0.93515 nm,c=0.67872 nm,α=β=90°,γ=120°,V=0.5138692 nm3.Three strong peaks located at 32.079o,32.595o,and 50.104o with d=2.7903,2.74649,1.8194 was in accordance with,(112),and(213) planes.The optimum concentration of Tb3+ in Ca2Y8Si6O26 to yield highest photoluminescence intensity was 10 mol.% of Y3+.The corresponding excitation spectrum consisted of an intense broad band from 220 to 260 nm.The photoluminescence measurements showed that the green emission originated from 5D4-7F5 was predominant in the measured range with strong doublet lines at 543 and 549 nm. 相似文献
4.
5.
含Na2O-MgO添加剂自增韧Al2O3的研究 总被引:4,自引:0,他引:4
研究了Na2O-MgO系统添加剂的加入量对原位增强Al2O3陶瓷的显微结构和性能的影响规律.结果表明在实验的添加剂量范围内,适量的添加剂能促使β'-Al2O3柱状晶的形成,长径比增大,其强度和断裂韧性增加.并讨论了添加剂量对原位增强氧化铝陶瓷的显微结构和性能的影响机理. 相似文献
6.
以煤气为还原气,以Fe为活性金属催化还原冶炼烟气中SO2制取硫磺,研究了反应温度、反应时间、气配比及金属铁含量等对SO2还原成S单质的影响.结果表明:对SO2催化还原生成单质硫产率而言,最佳的反应温度为400℃,最佳气配比为0.75(即煤气:SO2烟气流量=30誜40).催化剂中金属Fe的最佳含量为14%,当反应温度为400℃时,14%Fe/Al2O3催化还原SO2反应的转化率为96.31%,生成单质硫选择性达到85.06%,而硫的产率为81.92%.所制硫磺色泽均匀,为淡黄色,纯度高达99%. 相似文献
7.
8.
用热重/差热(TG/DTA)分析法研究了粒度及升温速度对Sm2Fe17合金热稳定性的影响,结合XRD物相分析结果说明Sm2Fe17合金氧化过程中发生的化学反应,用Kinssinger法计算了Sm2Fe17合金被氧化所需的表观活化能并推断了其反应机理.结果表明:Sm2Fe17合金粉的粒度越细,其热稳定性越差;升温速度越快,Sm2Fe17合金的氧化温度增高,放出的热量减小.Kinssinger法计算Sm2Fe17合金在低温氧化时的表观活化能为162kJ·mol-1,在高温氧化时为189.8kJ·mol-1. 相似文献
9.
研究了一种采用非水溶液电解法与RTO金属包埋切片微米一纳米表征法联合分析钢中非金属夹杂物的新方法,该方法全过程对夹杂物不产生任何损伤破坏作用.通过夹杂物检测结果实例分析证明,该方法能够得到夹杂物表面和内部形貌及相组成的完整清晰信息. 相似文献