Epitaxial growths of the GaAs/AlGaAs-based 940 nm infrared light emitting diodes (LEDs) with dual junctions were carried out by using metalorganic chemical vapor deposition (MOCVD) with different doping concentrations and Al contents in AlxGa1-xAs compound. And their optoelectric properties show that the optimal design for tunneling region corresponds to P++ layer with hole concentration up to 1×1020 cm-3, N++ layer electron concentration up to 5×1019 cm-3 and constituent Al0.2Ga0.8As in the tunneling junction region. The optimized dual-junction LED has a forward bias of 2.93 V at an injection current of 50 mA, and its output power is 24.5 mW, which is 104% larger than that of the single junction (12 mW). Furthermore, the optimized device keeps the same spectral characteristics without introducing excessive voltage droop. 相似文献
3.
采用动电位极化、电化学阻抗谱(EIS)测试、浸泡实验、SEM和EDS分析研究了Cr的添加对铸态X52钢在湿H2S环境中腐蚀行为的影响。结果表明,Cr的添加,对阴极反应有显著的抑制作用,提高了铸态X52钢的耐蚀性。但耐蚀性并不总是随着Cr含量的升高而增强。Cr的添加对腐蚀产物的形貌有很大影响,使表面腐蚀产物由疏松多孔变为致密平整。内层富Cr腐蚀产物的出现,使腐蚀速率明显降低。 相似文献
4.
5.
某企业Mn13钢采用连铸工艺生产,轧制后出现批量沿中心面分层开裂的情况,且开裂比例远高于模铸坯料,初期试验证实这与坯料中心面附近粗大碳化物析出有关,因此重点研究Mn13钢连铸坯在凝固及冷却过程中碳化物的析出特征。本研究通过Thermo-calc热力学计算和实验室模拟冷却组织观察的方法研究了Mn13钢冷却过程中碳化物的析出行为,计算结果表明,在热力学平衡条件下,碳化物在847℃时开始析出,到557℃时碳化物全部析出。模拟冷却试验的组织观察结果表明,在冷却处理前(650℃以上)没有可见的碳化物析出;冷却至550℃时碳化物开始明显析出,400~550℃为碳化物析出的敏感温度区间。在生产过程中,连铸坯在400~550℃温度区间应该选择快速冷却方式避免碳化物析出。此外,现场工艺实践表明,采用合理的连铸工艺(如钢水过热度、电磁搅拌及动态轻压下工艺)也有助于改善Mn13钢铸坯中心偏析问题,减轻铸坯凝固过程中芯部的碳化物析出倾向。 相似文献
6.
7.
介绍了50t/d市政污泥干化系统的湿污泥接收储存及输送、污泥干化机、干污泥输送、蒸汽供应及凝结水回收、尾气处理、臭气收集输送等装置设备及设计,对市政污泥干化系统的研发和优化具有借鉴意义。 相似文献
8.
不锈钢具有光亮洁净的表面和良好的耐腐蚀性能,研究了退火温度对不锈钢酸洗难易程度的影响,通过理论分析和实际生产数据分析,以304钢种为例进行模拟实验,验证其影响规律。 相似文献