Effect of temperature on mechanical behavior of AZ31 magnesium alloy

Strain rate sensitivity and tension/compression asymmetry of AZ31 magnesium alloy at different temperatures and strainrates were investigated.Both of mechanical behaviors are temperature dependent.Strain rate sensitivity increases with increasingtemperature.Thermally activated slip is the source of strain rate sensitivity.At the temperature below or near 373 K,strain ratesensitivity is very little.Tension/compression asymmetry in yielding decreases with increasing temperature.Twinning is the reasonof tension/compression asymmetry.At the temperature above or near 573 K,the material shows little tension/compressionasymmetry of the flow stress.     

α相含量对新型亚稳β钛合金动态力学性能的影响

通过对2A2F(Ti-2Al-9.2Mo-2Fe-0.1B)钛合金在相变点以下进行固溶处理,使用扫描电镜和电子背散射衍射对处理后的显微组织与其在高应变率条件下的动态力学性能的关系进行了研究.结果表明,在650～790℃范围内,随着固溶温度的升高,实验合金组织中初生α相减少,动态流动应力降低,均匀塑性应变升高.经650℃...     

冲击载荷作用下AZ31镁合金中的变形局域化

为了揭示镁合金在高应变率载荷作用下容易发生变形局域化的机理,采用分离式Hopkinson杆对AZ31镁合金进行冲击压缩和拉伸试验,而后对冲击后的试样进行变形机制分析.分析表明:镁合金的变形局域化区域也和钛合金等材料中的绝热剪切带区域一样由细小晶粒组成,但是这种细小晶粒不是由于动态再结晶所致,而是由大致相同的连接成线的晶体学取向的晶粒在外载荷作用下大量孪生变形造成的.     

AZ31镁合金表面液相渗铝的工艺与性能

采用液相扩渗技术在挤压态AZ31镁合金表面快速渗入铝，在合金表面获得过共晶渗层，并对渗层的成分、相组成、扩渗过程、纳米硬度和腐蚀性能进行分析。结果表明：AZ31镁合金在480℃热扩渗铝过程中发生了“熔化—凝固”变化，渗层为典型的过共晶组织：渗铝层含有Mg17A112相和镁的铝饱和固溶体，这种渗层具有较高的纳米硬度和较好的耐腐蚀性能；通过提高扩渗温度进行液相扩渗可以大大提高扩渗速度，但由于快速凝固收缩会造成表层产生起伏现象，控制冷却速度可以将表层起伏控制在可接受的范围。     

冷轧Cu板动态压缩力学性能各向异性的研究

利用Instron电子拉伸机和Split-Hopkinson压杆(SHPB)实验装置,研究了准静态和动态压缩条件下冷轧和退火Cu板法向、轧向、横向的力学性能.不同应变率下的应力-应变曲线表明:冷轧和退火Cu板的流变应力均随应变率的增加而增加,表现出明显的应变率强化效应.冷轧Cu板准静态和动态压缩力学性能均呈现明显的各向异性:横向屈服强度最大,轧向最小,且低应变程度下的流变应力也具有同样规律.退火Cu板呈现近似各向同性.考虑准静态和动态变形时可能的塑性变形机制,基于微观晶体塑性变形理论的Taylor模型可定性地解释冷轧Cu板压缩力学性能的各向异性.     

Deformation behavior ofAZ31 magnesium alloy at different strain rates and temperatures

The deformation behavior of AZ31 was examined by compression and tension testes over a wide strain rate and temperature range, strain rate from 10^-3 to 10^3 s^-1, temperature from 300 to 623 K. Analysis of flow behavior and microstructural observations indicate that in tension tests dislocation glide is the most important deformation mechanism in the test strain rate and temperature range, while in compression tests twinning deformation mechanism is important at lower temperature when the strain rate ranges from 10^-3 to 10 s^-1. At 10^3 s^-1 strain rate, dislocation glide and twinning are present at the same time. At the strain rate of 2 964 s^-1, adiabatic shear band can be found easily, even at the strain rate of 1 537 s^-1 adiabatic shear localization zone can be found. In adiabatic shear localization zone, there are fine recrystallization grains. But in adiabatic shear band, the grains cannot be identified by optical microscopy.     

热轧TB2钛合金织构多晶板动态压缩性能的各向异性

利用Instron 电子拉伸机和分离式霍普金生压杠(SHPB)实验装置, 研究了准静态和动态压缩条件下热轧TB2钛合金织构多晶板的力学性能。对TB2钛合金板材的轧向、横向以及轧制平面内与轧向成45°等3个方向进行了压缩实验, 得到了不同应变速率下的应力-应变曲线。结果表明：热轧TB2钛合金板材不同方向上的流变应力均随应变速率的增加而增加, 表现出明显的应变速率强化效应。准静态和动态力学性能均表现出各向异性, 且准静态和动态压缩行为规律不一致。考虑准静态和动态变形时可能的塑性变形机制, 基于微观晶体塑性变形理论, 定性讨论了热轧织构多晶TB2钛合金板屈服强度的各向异性     

Plastic deformation mechanisms ofAZ31 magnesium alloy under high strain rate compression

The twinning and slip activities of AZ31 magnesium alloy sheet at a strain rate of 1 200 s^-1 were investigated. Dynamically mechanical properties of various oriented samples were measured using Split Hopkinson Pressure Bar（SHPB）. Optical microscope observations reveal that the dominant deformation mechanism is twinning for 90° oriented sample, and is slip for 45° and 0° oriented samples. TEM analysis for samples at a strain of 0.3% shows that the main deformation mechanisms for 90°, 45° and 0° oriented sample are {1012} 〈 1011 〉 and {1011} 〈 1012 〉 twinning, basal slip and non basal slip, respectively. The main features of the true stress--true strain curves can be explained based on deformation mechanism analysis.     

镁合金表面电弧喷涂纯铝的界面特性研究

采用电弧喷涂技术对ZK60和AZ91两种镁合金表面喷铝,为了提高界面结合性能,对喷后样品进行了真空条件下450℃保温2h和250℃真空热压1h两种不同的后处理,结果表明:两种处理工艺都能一定程度的提高界面性能,但是前一处理工艺基体晶粒显著长大,后一处理工艺则对基体的影响较小,并且同时改善了涂层自身的性能.     

冲击加载条件下AZ31B镁合金变形孪晶的微观特征

采用分离式Hopkinson压杆(SHPB)对A231B热轧板材沿轧向进行冲击实验,加载应变率约为1200 s-1．利用金相显微镜和透射电子显微镜观察微观组织特征。结果表明：在应变量约为0.003的条件下,压缩孪生{10?1}/<10?2>与拉伸孪生{1?02}/< 1?01>均为孪生塑性变形机制,这与准静态加载下单一的拉伸孪生机制不同。孪晶内部的微观特征演化过程包括：1）平行排列基面层错的出现;2）与孪晶界成特定角度平行排列位错线的形成;3）位错胞的产生。