A new high-strength aluminum alloy with better fluidity than that of ZL205A was developed. The effect of applied pressure during squeeze casting on microstructures and properties of the alloy was studied. The results show that the fluidity of the alloy is 16% and 21% higher than that of ZL205A at the pouring temperature of 993 K and 1 013 K, respectively. Compared with permanent-mold casting, mechanical properties of the alloy prepared by squeeze casting are much higher. The tensile strength and elongation of the alloy are 520 MPa and 7.9% in squeeze casting under an applied pressure of 75 MPa, followed by solution treatment at 763 K for 1 h and at 773 K for 8 h, quenching in water at normal temperature and aging at 463 K for 5 h. The improvement of mechanical properties is attributed to the remarkable decreasing of the secondary dendrite arm spacing(SDAS) and eliminating of micro-porosity in the alloy caused by applied pressure. 相似文献
2.
铝合金铸件充型过程及氧化膜卷入的数值模拟 总被引:2,自引:0,他引:2
对于直接有限差分法,提出了单元表面无量纲距离、表面充填比率和体积充填比率,以描述铸件充型过程中自由表面的形状,建立了相应的充型过程数学模型,考虑了自由表面形状对动量、质量和能量传输的影响;提出了充型过程自由表面碰撞中表面氧化膜破碎,及其后破碎氧化膜流动的计算模型。对实验铝合金铸件进行了模拟应用,通过实际铸件充型过程的特殊X射线实时观察和记录。及实际铸件的气孔、收缩缺陷分布的检测,对模拟结果进行了验证分析。结果表明:充型过程模拟结果与X射线实时观察结果吻合较好,尤其是自由表面的变化;氧化膜卷入模拟结果与实际铸件气孔、收缩缺陷的分布存在一定的对应关系。 相似文献
3.
4.
5.
6.
综合现阶段国内外FRP复合材料加固砌体结构的研究现状,并结合工程实际案例,就FRP复合材料加固砌体结构的选材、加固设计及加固施工等方面的相关注意事项,作了有重点的阐述,内容涉及FRP选材要点、FRP强度有效利用值、对火灾等极端因素的考虑、墙体单面加固的有效性等诸多方面,相关经验可供工程实际参考使用。 相似文献
7.
Al-7Si-Mg铝合金挤压铸造过程热-力行为的研究 总被引:1,自引:0,他引:1
采用了0.1、50、75和100 MPa压力对Al-7Si-Mg合金进行直接挤压铸造,对铸型内温度和压力变化进行了测试,讨论了两者之间的关系以及压力变化对收缩缺陷形成的影响。同时,计算了凝固过程铸件和模具界面摩擦力。结果表明,外挤压力对界面摩擦力和压力传递有重要作用。 相似文献
8.
9.
10.
挤压铸造Al-5Cu合金的组织与性能 总被引:1,自引:1,他引:1
使用挤压铸造工艺制备出一种新开发的、高强韧Al-5Cu合金,在50 MPa挤压力下铸造成型后,进行T4和T5热处理.经固溶处理后其抗拉强度达472 MPa,伸长率达10.5%.并对热处理状态下的组织和性能进行了分析研究. 相似文献