在对系列La 掺杂的Bi2Sr2 - xLaxCuO6 + δ单晶的研究中,我们发现在极度La 掺杂( 空穴极度欠掺杂) 的样品中有高达36K 的超导相出现.X 射线衍射图(XRD) 和电镜照片都表明这种极度空穴欠掺的样品有很好的单相性,从而排除了样品化学不纯的可能.另外,对这种样品进行脱氧处理后,此超导电性相应消失,说明了这种高Tc 的超导电性是由活动性空穴掺杂引起的.虽然对相应样品在正常态的磁测量没有测出反铁磁峰(Neel 峰) ,但对系列样品的拉曼散射研究发现样品随着La 含量的增多,其反铁磁交换作用明显加强.所以,我们认为这种高Tc 超导电性的出现是在Bi2201 体系中存在宏观相分离的明显迹象 相似文献
3.
Superconducting La1.937Sr0.063CuO4 crystals grown by the travelling-solvent floating-zone technique were thermally treated under various temperatures and oxygen pressures for moderately adjusting the oxygen content. The response of intrinsic electronic property of the crystals to the change of hole density in La2-xSrxCuO4 in the vicinity of the magic doping of x= 1/16 (= 0.0625) is studied in detail by magnetic measurements under various fields up to 1 T. It is found that when the superconducting critical temperature (Tc) increases with the oxygen content, there appears also a new subtle electronic state that can be detected from the differential curves of diamagnetic susceptibility dx/dT of the crystal sample. In contrast with the intrinsic state, the new subtle electronic state is very fragile under the magnetic fields. Our results indicate that a moderate change in oxygen doping does not significantly modify the intrinsic electronic state originally existing at the magic doping level. 相似文献
4.
The effects of interstitial oxygen on superconducting electronic phases in strontium and oxygen co-doped La1.937Sr0.063CuO4+δ 下载免费PDF全文
Strontium and oxygen co-doped La1.937Sr0.063CuO4+δ superconductor with Tc≈ 40K, which is obtained by oxidizing strontium-doped starting ceramic sample La1.937Sr0.063CuO4 in NaC10 solution, is annealed under different conditions to allow interstitial oxygen to redistribute. The evolution of the intrinsic superconducting property with the oxygen redistribution is studied in detail by magnetic measurements in various fields. It is found that there occurs the electronic phase separation from the single superconducting phase with Tc ≈ 40 K into two coexisting superconducting states with values of Tc: 15 and 40K or of 15 and 35 K in this system, depending on annealing condition. Our results indicate that the 15, 35 and 40 K superconducting phases associated with the excess oxygen redistribution are all thermodynamically meta-stable intrinsic states in this Sr/O co-doped cuprate. 相似文献
5.
报道了系列欠掺杂La2-xSrxCuO4(x=0063,0070,0 090,0110,0125)单晶的零场和加磁场情况下ab面和c方向的热导率与温度的关系曲线,测量 温度范围从2到45K. 研究发现ab面和c方向的热导率都受到磁场的压制. 而且在磁场 的作用下,热导压制率随温度变化的关系和场致反铁磁有序的增强与温度的依赖关系有高度 相似性. 认为磁场引起的ab面的热导压制主要是电子热导的变化所致,而c方向的 压制则可能主要来源于声子热导的变化,它们均可能与磁场诱导下欠掺杂La2-x SrxCuO4的某种电荷有序和磁有序的增强密切相关.
关键词:
热导
电荷有序
磁有序 相似文献
6.
通过X射线衍射、差热分析、电子显微镜、超导电性测量等手段研究了研磨对Y-123和Bi(Ph)-2223超导相和成相过程的影响。结果表明:研磨对Y-123和Bi(Ph)-2223超导相的影响显著不同,研磨导制了Bi(Ph)-2223超导相的破坏。同时指出Bi(Ph)-2223超导相同一结构特征的两种属性:好的可塑性和结构易破坏性。前者是优点,后者是缺点。在加工、测量、使用过程中,要尽力避免后一缺点带来的超导电性的破坏或由于局部结构破坏而导致的整体性能的降低。 相似文献
7.
8.
用电泳法在MgO基底上制备YBCO超导厚膜 总被引:1,自引:0,他引:1
电泳方法具有工艺简单,成本低廉,基底的形状和尺寸不受限制,膜厚容易控制的特点.本文采用电泳方法在00l取向的MgO基底上制备高温超导YBCO厚膜.在后退火过程中,采用籽晶诱导熔融生长法,成功制备转变温度约85K,转变宽度约3K的YBCO超导厚膜.X射线衍射结构分析揭示了在MgO基片上生长的样品绝大部分都是Y123相c轴取向的晶粒,少部分是Y211相的晶粒.此结果与通过扫描电子显微镜观察膜表面的形貌得到的结论是一致的.通过扫描电子显微镜的剖面图,可以看到生长非常清晰紧凑的,厚度约30μm的YBCO膜层.所制备YBCO厚膜样品用磁滞回线法估算其最高临界电流密度为0.978×103A/cm2,高于文献中用电泳法制备YBCO厚膜的最高临界电流密度. 相似文献