Study on the in—plane electrical resistivity and thermoelectric power in single crystals of La2—xBaxCuO4

The in-plane electrical resistivity and thermoelectric power have been measured on single crystals of La_2-xBa_xCuO₄ at around x=0.125. The room temperature resistivity and thermopower have their maximum values at x=0.125, indicating that the carrier concentration is the minimum and the carriers are most strongly localized at x=0.125. The observed semiconductor-like behaviour can be well described by the weak-localized quasi-two-dimensional state. The steep rise in electric resistivity of the sample at x=0.125 below 70K is attributed to the formation of static stripe-order of holes and spins, which are pinned by the low-temperature tetragonal (LTT) structure, as discovered in La_1.48Nd_0.4Sr_0.12CuO₄. The temperature dependence of electric resistivity below 70K is still well described by the formula ρ∝ lnT. A definite change in the slope of thermopower is observed at the low-temperature orthorhombic-LTT structural phase transition temperature. The origin of the 1/8 anomaly is discussed in the text.     

Sm2-xCexCuO4的物性研究

制备了Sm2-xCexCuO4的多晶样品.X-射线粉末衍射结果表明,该系列样品为K2NiF4214结构,当0.090.17时,为T'相.电阻率测量在0.15,0.17,0.19样品上观测到超导转变.最高Tc对应于x=0.17为13.6K,均远低于(Pr0.8La1.2)1.85Ce1.2CuO4 的超导转变温度(30K).这是由于该系列样品在远高于超导转变温度时就存在更强的载流子局域化效应.磁化率测量结果表明x=0.17的样品为体超导.该体系样品的Tc低、抗磁信号小与载流子的强局域化效应有关.热电势测量结果表明,在最佳超导组份附近斜率改变符号,欠掺杂区域载流子为电子型,过掺杂区域载流子为空穴型.     

高纯度超导氧化物RuSr2GdCu2O8的合成与超导电性

RuSr2GdCu2O8据报道是转变温度为30－40K的超导体，其合成的主要问题是，在合成过程中有相当多的铁磁性的SrRuO3杂相伴随着主相一起生成，本文报道了合成RuSr2GdCu2O8（Ru-1212相）纯相的新方法，即在O2和水蒸气气氛中首先合成纯相的Sr2GdRuO6(Ru-211相）先驱物，然后Sr2GcRuO6与CuO高温烧结，生成RuSr2GdCu2O8。合成的RuSr2GdCu2O8电阻为半导体温度行为，该体系的超导转变与生成的杂相有关。     

电子型超导体Sm1.85Ce0.15CuO4单晶的赝能隙行为研究

测量了在O2中退火不同时间的Sm1.85Ce0.15CuO4单晶样品的热电势S与电阻率ρ的温度依赖关系.所有的样品电阻率高温下呈现线性温度依赖行为.未退火的样品在148K发生超导转变,而退火后的样品在低温下发生金属半导体相变,其超导电性消失,表明退火引起了载流子浓度下降,体系进入欠掺杂态.随着温度降低,所有的样品ST和ρT曲线在200K附近(T)都发生斜率的改变,可以用赝能隙现象解释.热电势S在低温下出现一个正的曳引峰,意味着载流子符号发生改变,由电子型转变为空穴型 关键词： 电子型超导体 热电势 赝能隙     

电子型超导体Nd1.85Ce0.15CuO4单晶输运性质研究

我们测量了最佳掺杂的Nd1．85Ce0．15CuO4单晶的电阻率和ab面以及c方向热电势．ρ-T曲线在高温下表现为非常好的直线，超导转变比较尖锐Tc,mid=20．6K，说明我们的样品品质很好．低温下的电阻率拟合结果表明频率大约100K的软声子模与载流子有强烈相互作用，这是极化子模型有力的证据．对于热电势结果，令人惊奇的是，无论数值还是曲线形状，包括低温曳引峰的位置，c方向的热电势Sc与ab面内的热电势Sab非常接近．这可能是某种共同的机制导致的结果．比较Nd1．85Ce0．15CuO4和Sm1.85Ce0.15CuO4的热电势曲线可以发现，二的数值和曲线形状基本相同，而与La1．85Sr0．15CuO4差异较大，这进一步说明了顶点氧在这些体系中的作用．     

电子型超导体Sm1.85Ce0.15CuO4单晶样品的制备和品质鉴定

本研究了助溶剂法生长了Sm2-xCeXCuO4单晶的可行性，制备出x=0.15,Sm2-x=CexCuO4单晶，并作了品质鉴定，为了研究坩埚中的Al掺入的情况，对电阻率和热电势进行了测量。     

(La1-xSmx)0.185Sr0.15CuO4的输运性质的研究

通过对系列（La1-xSmx)0.185Sr0.15CuO4（x=0,0.05,0.10,0.15)的多晶样品在4.2K-300K的电阻率和液氮温区内的热电势的测量,发现（La1-xSmx)0.185Sr0.15CuO4的电阻率在高温区呈现出线性关系,其斜率也随着x的增大而增大,在x=0.10时达到最大,而在Tc到100K的温区,随着Sm含量的增加,则呈现出由金属行为到类半导体行为的转变,同时超导温度Tc也随着降低,液氮温区内的温差热电势反映了随着Sm含量的增加,体系的载流子浓度也随之降低。     

新型超导体MgB2的热电势和电阻率研究

测量了MgB₂的热电势和电阻率与温度的依赖关系.在100K—300K区间,热电势呈近似线性温度依赖关系,其斜率为正,表明载流子为空穴型且与能带贡献的图像相一致.与此对应,在此温区电阻率呈T²依赖关系.在100K以下,热电势和电阻率各自转变了其高温区的温度依赖关系.热电势在超导转变温度T_c(零电阻366K)到100K间有一宽峰,具有声子曳引峰的特征,表明电子-声子相互作用很强.估算了一些重要的参数,如带米能E_F、能带宽度 关键词： 新型超导体 热电势 电阻率     

电子型超导体Sm2-xCexCuO4(0.00≤x≤0.21)的异常热电势与电阻率

测量了Sm2-xCexCuO4(0.00≤x≤0.21)多晶样品的热电势S和电阻率ρ的温度依赖关系.在缘绝体-金属转变边界处,观测到热电势从绝缘体区明显的弱温度依赖关系到金属区线性温度依赖关系的转变.当Ce的含量由0.09增加到0.21时,高温下S的斜率发生由负到正的转变,这是能带的填充能级发生改变时电子型和空穴型载流子的贡献发生竞争的表现,由电子型向空穴型的过渡发生在x＝0.17处.S和ρ在200K以下的斜率变化是载流子局域化造成的.x＝0.06-0.21的样品在50K处观察到一个正的曳引峰.室温下的热电势S300K和S0(高温区热电势线性外推到0K的值)与Ce含量在绝缘体、欠掺杂和过掺杂区域有不同的依赖关系.过掺杂区域很小的S300K和S0意味着一个宽带的费米液体的贡献,同时ρ满足T2关系,二者相一致.     

Abnormal magnetic behaviors induced by the antisite phase boundary in LaeNiMnO6

The ferromagnetic semiconductor La2NiMnO6 （LNMO） has recently received much attention due to its high Curie temperature （Tc 280 K）, which is close to room temperature. We prepared single-phase LNMO polycrystaUine samples and investigated the temperature- and field-dependent magnetic behaviors of bulk LNMO. Between Tc and T＊ = 300 K, we observed upward and downward deviations from the Curie-Weiss law for high and low magnetic fields, respectively. From the electron spin resonance results, we can exclude the existence of the Griffiths phase. On the contrary, our results indicate that the abnormal magnetic behaviors might be induced by antisite phase boundaries with antiferromagnetic interaction.