1.
为了研究Mg ,Al掺杂对锂二次电池正极材料LiCoO2 体系的电子结构的影响 ,进而揭示Mg掺杂的LiCoO2 具有高电导率的机理 ,对Li(Co ,Al)O2 和Li(Co,Mg)O2 进行了基于密度泛函理论的第一原理研究 .通过对能带及态密度的分析 ,发现在Mg掺杂后价带出现电子态空穴 ,提高了电导 ,并且通过歧化效应 (disproportionation)改变了Co 3d电子在各能级的分布 ,而Al掺杂则没有这些作用 .O2 - 的离子性在掺杂后明显增强 . 相似文献
2.
The effects of Zn vacancies on ferromagnetism in Cu-doped ZnO films controlled by oxygen pressure and Li doping 下载免费PDF全文
Zn0.99Cu0.01O films were studied experimentally and theoretically.The films were prepared by pulsed-laser deposi tion on Pt(111)/Ti/SiO2/Si substrates under various oxygen pressures to investigate the growth-dependence of the ferromag netic properties.The structural,magnetic,and optical properties were studied,and it was found that all the samples possess a typical wurtzite structure,and that the films exhibit room-temperature ferromagnetism.The sample deposited at 600℃and an oxygen pressure of 10 Pa showed a large saturation magnetization of 0.83μB/Cu.The enhanced ferromagnetism in the(Cu,Li)-codoped ZnO is attributable to the existence of Zn vacancies(VZn),as shown by first-principles calcu lations.The photoluminescence analysis demonstrated the existence of V Zn in both Zn0.99Cu0.01O and(Cu,Li)-codoped ZnO thin films,and this plays an important role in the increase of ferromagnetism,according to the results of first-principles calculations. 相似文献
3.
4.
Co2FeAl0.5Si0.5 (CFAS)-based multilayers sandwiched by MgO layers have been deposited and annealed at different temperatures. Perpendicular magnetic anisotropy (PMA) with the magnetic anisotropy energy density Ku ≈2.5×106 erg/cm3 (1 erg = 10-7 J) and the coercivity Hc = 363 Oe (1 Oe = 79.9775 A · m-1) has been achieved in the Si/SiO2/MgO (1.5 nm)/CFAS (2.5 nm)/MgO (0.8 nm)/Pt (5 nm) film annealed at 300 ℃. The strong PMA is mainly due to the top MgO layer. The structure can be used as top magnetic electrodes in half-metallic perpendicular magnetic tunnel junctions. 相似文献
5.
6.
7.
以LiNO3和Co(NO3)2为主要原料、采用溶胶-凝胶旋涂法在(111)单晶硅片上制备了LiCoO2薄膜.X射线衍射结果表明,涂液中Li+离子和Co2+离子的总浓度与配比可影响薄膜的成分.薄膜的最佳烧结温度与最佳烧结时间分别为600~700℃和30~60min.涂液中柠檬酸、聚乙烯乙二醇、去离子水的含量与热处理时的升温速率对薄膜的形貌有很大影响. 相似文献
8.
Spin pumping at the Co2FeAl0.5Si0.5/Pt and Pt/Co2FeAl0.5Si0.5 interfaces has been studied by ferromagnetic resonance technology(FMR). The spin mixing conductance of the Co2FeAl0.5Si0.5/Pt and Pt/Co2FeAl0.5Si0.5 interfaces was determined to be 3.7×1019m 2and 2.1×1019m 2 by comparing the Gilbert damping in a Co2FeAl0.5Si0.5single film, Co2FeAl0.5Si0.5/Pt bilayer film and a Pt/Co2FeAl0.5Si0.5/Pt trilayer film. Spin pumping is more efficient in the Co2FeAl0.5Si0.5/Pt bilayer film than in permalloy/Pt bilayer film. 相似文献
9.
Magnetic properties of a Pt/Co<sub>2</sub> FeAl/MgO structure with perpendicular magnetic anisotropy 下载免费PDF全文
Microstructures and magnetic properties of Ta/Pt/Co 2 FeAl(CFA)/MgO multilayers are studied to understand perpendicular magnetic anisotropy(PMA) of half-metallic full-Heusler alloy films.PMA is realized in a 2.5-nm CFA film with B2-ordered structure observed by a high resolution transmission electron microscope.It is demonstrated that a high quality interface between the ferromagnetic layer and oxide layer is not essential for PMA.The conversions between in-plane anisotropy and PMA are investigated to study the dependence of magnetic moment on temperature.At the intersection points,the decreasing slope of the saturation magnetization(M s) changes because of the conversions.The dependence of M s on the annealing temperature and MgO thickness is also studied. 相似文献
10.