Electrochemical Deposition and Properties of ZnTe Nanowire Array

Pulsed electrodeposited technique is applied to fabricate ZnTe nanowire arrays with different diameters into the anodic alumina membrane in citric acid solution. The x-ray powder diffraction, scanning electron microscopy and transmission electron microscopy indicate that the high ordered, uniform and single-crystalline nanowires have been fabricated. The optical absorption spectra of the nanowire array show that the optical absorption band edge of the ZnTe nanowire array exhibit a blue shift compared with that of bulk ZnTe, and the nonlinear current-voltage characteristic is observed.     

镀镍石墨粉与铜基自润滑材料摩擦磨损特性研究

采用粉末冶金复压复烧工艺制备铜基石墨复合材料,考察了不同载荷条件下铜基石墨复合材料的摩擦磨损性能.结果表明:在载荷20～60 N条件下,含6%(质量分数)石墨的铜基复合材料经历了轻微磨损、中等磨损到严重磨损3个过程;石墨颗粒表面镀镍可以提高石墨与铜合金基体的界面结合强度以及磨损过程中所形成的转移层与基体间的粘附性能,含6%镀镍石墨的铜基复合材料的自润滑性能得到改善,只经历了轻微磨损和中等磨损2个过程.     

石墨对铜基自润滑材料高温摩擦磨损性能的影响

通过基体多元合金化和选用不同粒度的石墨颗粒,采用常规粉末冶金方法制备了铜基石墨固体自润滑材料,在大越式OAT-U型摩擦磨损试验机上考察了复合材料从室温到500℃温度条件下的摩擦磨损性能,利用扫描电子显微镜观察分析磨损表面形貌,进而探讨其摩擦磨损机理.结果表明:在室温条件下,石墨颗粒越小,则复合材料的摩擦系数越小,减摩自润滑效果越好;在室温至500℃条件下,选用合适的石墨粒度(0.3～0.5mm)和多元基体合金化,可使铜基石墨固体自润滑材料保持较好的自润滑特性.     

电沉积制备磁性纳米线的研究进展

多孔阳极氧化铝为模板制备纳米结构材料具有独特的优越性,颇受人们的关注,近年来获得了深入的研究.文章介绍了用电化学沉积方法制备一维磁性纳米线的最新研究进展,阐述了各种结构磁性纳米线,包括单质、合金、多层、超晶格磁性纳米线的研究现状,展望了磁性纳米线的研究方向和在高密度垂直磁记录与巨磁电阻等方面的应用前景.     

电沉积二氧化钛功能薄膜的制备与组织转变研究

采用直流电沉积方法,在石墨板上成功制备了半导体二氧化钛功能薄膜前驱体,分析讨论了电沉积过程中实验参数对TiO2前驱体成膜的影响,获得了制备二氧化钛膜最佳工艺参数.TiO2前驱体沉积速率随着电流密度的增大而增加,为了保证薄膜质量,将电流密度控制在5～45mA/cm2之间;溶液浓度对沉积速率也有影响,当溶液中TiCl4:H2O2=1:2时沉积速率最大;最佳沉积温度为5-10℃.运用差热分析、XRD相结构分析和SEM等手段,研究了该前驱体到锐钛矿相(anatase)和金红石相(rutile)二氧化钛的组织相转变过程,300℃热处理得到锐钛矿相的二氧化钛,650℃热处理后出现金红石相.     

碳纳米管负载纳米TiO2复合材料的制备及其性能

采用溶胶-凝胶法, 以钛酸丁酯为原料, 将纳米TiO2负载在碳纳米管(CNTs)表面, 制备了CNT-TiO2光催化复合材料. 通过X射线衍射(XRD)、透射电子显微镜(TEM)等手段研究了复合颗粒的形态结构及包覆情况, 通过UV-Vis漫反射谱分析比较了纯TiO2和CNT-TiO2的吸光性能, 并研究了不同温度热处理的CNT-TiO2光催化剂在紫外光照射下对甲基橙光催化降解的性能. 结果表明, 纳米TiO2颗粒以锐钛矿相存在, 紧密地包附在碳纳米管的管壁上, CNT-TiO2在紫外-可见光波长范围内均有较好的吸光性能, 450 ℃热处理后的复合光催化剂CNT-TiO2比纯TiO2对甲基橙光降解有更高的光催化活性.     

硒化银纳米枝晶的合成与表征(英)

Silver selenide nanodendrites were synthesized by the reaction of AgNO₃ and sodium selenosulfate in the presence of cetyltrimethyl ammonium bromide (CTAB). The as-synthesized sivler selenide samples were characterized by XRD, TEM and SAED. The results showed that Ag₂Se nanodendrites were of single crystalline with diameters ranging from 60～150 nm.     

Composition Dependent Magnetic Properties of Ni-Co-P Coated Carbon Nanotubes

用化学镀方法在碳纳米管表面沉积了具有不同镍/钴成分配比的镍钴磷合金层．讨论了Co²⁺与Ni²⁺的浓度比、镀液温度、pH值对沉积速率的影响．并利用场发射扫描电镜、透射电镜、X射线衍射仪、能谱仪和磁性测量仪对镍钴磷包覆碳纳米管进行了系统的结构和性能表征．结果表明：当镀液中Co²⁺与Ni²⁺的浓度比为1,pH值为9时沉积速率最大;镀液温度的升高会使沉积速率增大．磁性测试结果显示碳纳米管表面镀覆Ni-Co-P镀层后,其磁性能对镀层中的Ni、Co相对含量有强烈的依赖性．当Co²⁺: Ni²⁺=2:1时,饱和磁化强度最大．矫顽力分别在Co²⁺: Ni²⁺=1:2和Co²⁺: Ni²⁺=4:1时有2个峰值; 而磁导率分别在Co²⁺: Ni²⁺=1:4和Co²⁺: Ni²⁺=4:1时有2个峰值．     

非调质钢35MnVN强化状态的磨粒磨损性能研究

利用销－盘式ＭＬ－１０型磨粒磨损试验机，对非调质钢３５ＭｎＶＮ强化状态（淬火＋低温回火）的磨粒磨损性能进行了试验研究．结果表明，非调质钢３５ＭｎＶＮ强化状态的硬度虽然比调质处理的４０Ｃｒ钢和４５＃钢的都低，但因其显微组织中的沉淀相对提高耐磨性十分有益，而且晶粒细化也有利于提高耐磨性，所以在同样的试验条件下，非调质钢３５ＭｎＶＮ强化状态的耐磨粒磨损性能与４０Ｃｒ钢及４５＃钢调质处理后强化态的耐磨粒磨损性能基本相当，可以替代后二者在磨粒磨损工况下使用     

非调质钢35MnVN强化状态的磨料磨损性能研究

利用销－盘式ＭＬ－１０型磨粒磨损试验机，对非调质钢３５ＭｎＶＮ强化状态的磨粒磨损进行了试验研究，结果表明，非调质钢３５ＭｎＶＮ强化状态的硬度虽然比调质处理的４０Ｃｒ钢和４５＃钢的都低，但因其显微组织中的沉积相对提高耐磨性十分有益，而且晶粒细化也有利于提高耐磨性，所以在同样的试验条件下，非调质钢３５ＭｎＶＮ强化状态的耐磨粒磨损性能与４０Ｃｒ钢及４５＃钢调质处理后强化态的耐磨粒磨损性能基本相当，可以替