Experimental studies of the bond response of three-wire strands and some influencing parameters

The bond behavior of prestressing strands is of great importance for the capacity of precast prestressed concrete structures. In the present study, the bond behavior of three-wire strands, and some influencing parameters, were examined by means of steel encased pull-through and push-in tests. The three mechanisms: adhesion, friction and other mechanical actions were found to be present at the strand-concrete interface at different slip values. The results from the experiments showed that the micro roughness of the strand surface strongly affected the initial bond response of the strand, that is the adhesion in the interface. The maximum bond capacity of indented three-wire strands was found to be directly connected to the geometric properties of the strand indents. The influence of the concrete strength on the bond capacity of the strand was hard to interpret. However, the density of the concrete matrix was found to be a better parameter for determine the influence of the concrete rather than the compressive strength.     

The anisotropic effect of a weak magnetic field on the photoconductivity of C<Subscript>60</Subscript> single crystals

The effect of crystal orientation on the photogeneration of free charge carriers was studied for C₆₀ single crystals in a weak magnetic field. The photoconductivity sharply depends on the orientation of magnetic field with respect to the crystallographic directions, showing a 5–8% increase for seven axes of the C₆₀ crystal.     

Thermodynamic stability of GaInSb,InAsSb, and GaInP epitaxial films

The miscibility gaps and the critical temperatures of spinodal decomposition of ternary semiconducting Ga-In-Sb, Ga-In-P, and In-As-Sb systems are calculated by taking into account the deformation energy and the effect of plastic relaxation caused by the misfit dislocations. It is shown that taking into consideration elastic energy narrows the ranges of spinodal decomposition and lowers its critical temperature. The introduction of the phenomenological parameter into Matthews-Blakeslee formula makes it possible to reach a satisfactory agreement between theoretically calculated values of critical thickness of epitaxial films and the experimental data.     

Electrochemical synthesis and characterization of chloride doped polyaniline

Chloride doped polyaniline conducting polymer films have been prepared in a protic acid medium (HCl) by potentiodynamic method in an electrochemical cell and studied by cyclic voltammetry and FTIR techniques. The FTIR spectra confirmed Cl^- ion doping in the polymers. The polymerization rate was found to increase with increasing concentration of aniline monomer. But the films obtained at high monomer concentration were rough having a nonuniform flaky polyaniline distribution. Results showed that the polymerization rate did not increase beyond a critical HCl concentration. Cyclic voltammetry suggested that, the oxidation-reduction current increased with an increase in scan rate and that the undoped polyaniline films were not hygroscopic whereas chloride doped polyaniline films were found to be highly hygroscopic.     

High-efficiency LEDs of 1.6–2.4 µm spectral range for medical diagnostics and environment monitoring

High efficient LED structures covering the spectral range of 1.6–2.4 μm have been developed on the basis of GaSb and its solid solutions. The electroluminescent characteristics and their temperature and current dependences have been studied. The radiative and nonradiative recombination mechanisms and their effect on the quantum efficiency have been investigated. A quantum efficiency of 40–60% has been obtained in the quasi-steady mode at room temperature. A short-pulse optical power of 170 mW was reached. __________ Translated from Fizika i Tekhnika Poluprovodnikov, Vol. 37, No. 8, 2003, pp. 996–1009. Original Russian Text Copyright ? 2003 by Stoyanov, Zhurtanov, Astakhova, Imenkov, Yakovlev.     

1/f noise in large-area Hg<Subscript>1−x</Subscript>Cd<Subscript>x</Subscript>Te photodiodes

The 1/f noise in photovoltaic (PV) molecular-beam epitaxy (MBE)-grown Hg_1−xCd_xTe double-layer planar heterostructure (DLPH) large-area detectors is a critical noise component with the potential to limit sensitivity of the cross-track infrared sounder (CrIS) instrument. Therefore, an understanding of the origins and mechanisms of noise currents in these PV detectors is of great importance. Excess low-frequency noise has been measured on a number of 1000-μm-diameter active-area detectors of varying “quality” (i.e., having a wide range of I-V characteristics at 78 K). The 1/f noise was measured as a function of cut-off wavelength under illuminated conditions. For short-wave infrared (SWIR) detectors at 98 K, minimal 1/f noise was measured when the total current was dominated by diffusion with white noise spectral density in the mid-10⁻¹⁵A/Hz^1/2 range. For SWIR detectors dominated by other than diffusion current, the ratio, α, of the noise current in unit bandwidth i_n(f = 1 Hz, V_d = −60 mV, and Δf = 1 Hz) to dark current I_d(V_d = −60 mV) was α_SW-d = i_n/I_d ∼ 1 × 10⁻³. The SWIR detectors measured at 0 mV under illuminated conditions had median α_SW-P = i_n/I_ph ∼ 7 × 10⁻⁶. For mid-wave infrared (MWIR) detectors, α_MW-d = i_n/I_d ∼ 2 × 10⁻⁴, due to tunneling current contributions to the 1/f noise. Measurements on forty-nine 1000-μm-diameter MWIR detectors under illuminated conditions at 98 K and −60 mV bias resulted in α_MW-P = i_n/I_ph = 4.16 ± 1.69 × 10⁻⁶. A significant point to note is that the photo-induced noise spectra are nearly identical at 0 mV and 100 mV reverse bias, with a noise-current-to-photocurrent ratio, α_MW-P, in the mid 10⁻⁶ range. For long-wave infrared (LWIR) detectors measured at 78 K, the ratio, α_LW-d = i_n/I_d ∼ 6 × 10⁻⁶, for the best performers. The majority of the LWIR detectors exhibited α_LW-d on the order of 2 × 10⁻⁵. The photo-induced 1/f noise had α_LW-P = i_n/I_ph ∼ 5 × 10⁻⁶. The value of the noise-current-to-dark-current ratio, α appears to increase with increasing bandgap. It is not clear if this is due to different current mechanisms impacting 1/f noise performance. Measurements on detectors of different bandgaps are needed at temperatures where diffusion current is the dominant current. Excess low-frequency noise measurements made as a function of detector reverse bias indicate 1/f noise may result primarily from the dominant current mechanism at each particular bias. The 1/f noise was not a direct function of the applied bias.     

The Influence and Interpretation of Surface Parameters for Wetting Transitions in Ternary Mixtures

Starting from a microscopic Hamiltonian defined on a semi-infinite cubic lattice, and employing a mean-field approximation, the surface parameters relevant for wetting in confined ternary mixtures are derived. These are found in terms of the microscopic coupling constants, and yield a physical interpretation of their origins. In comparison with the standard expression for the surface free-energy density, several new terms arising from the derivation are identified. The influence of the surface parameters on a predicted unbinding transition in a mixture of oil, water, and amphiphile demonstrate that existing results are robust to the addition of the extra surface terms.     

Experimental characterisation of the drying effect on uniaxial mechanical behaviour of mortar

The main objective of this present study was to evaluate, for a standard mortar, the drying effect on its mechanical behaviour. Numerous uniaxial compression tests were thus performed with loading-unloading cycles. They were carried out on different samples previously preserved under various conditions of conservation: preserved from desiccation, air drying and rapid drying at 60°C. The obtained results showed significant influences of these conditions on the material behaviour (increase in strength, decrease in Young's modulus and Poisson's ratio) and the necessity of taking into account the coupling effects between mechanical—poromechanical behaviours and drying.     

Analysis of the mechanism of die soldering in aluminum die casting

A mechanism of soldering of an aluminum alloy die casting to a steel die is proposed. A soldering critical temperature is postulated, at which iron begins to react with aluminum to form an aluminum-rich liquid phase and solid intermetallic compounds. The liquid joins the die with the casting upon solidification. The critical temperature is determined by the elements in both the casting alloy and the die material and is equal to the solidus temperature of the resulting alloy. The critical temperature is used to predict the onset of die soldering, and the local liquid fraction is related to the soldering tendency. Experiments have been carried out to validate the concept and to determine the critical temperature for die soldering in an iron-aluminum system. Thermodynamic calculations are used to determine the critical temperature and soldering tendency for the cases of pure aluminum and a 380 alloy in a steel mold. Factors affecting the soldering tendency are discussed, and methods for reducing die soldering are suggested.     

Photosensitivity of surface barrier structures based on Cu(In,Ga)Se<Subscript>2</Subscript> films grown by codeposition in vacuum

Polycrystalline Cu(In,Ga)Se₂ (CIGS) films with various ratios of Cu, In, and Ga were grown by codeposition of all elements in vacuum. The X-ray diffraction study showed that the films are single-phase and possess a chalcopyrite structure with predominant [112] orientation. The films exhibited a mirror smooth surface and had a close-packed structure composed of crystallites with clear faceting and a transverse size of 0.1–0.3 μm. Related surface barrier structures of the (In,Ag)/Cu(In,Ga)Se₂ type were obtained and their spectra of the quantum efficiency of photoconversion were studied. The obtained structures can be used for optimization of the CIGS film technology.