研究了Sn-Cu-Ni(-Ce)焊点在长时间热循环条件下的力学性能,以及热循环对焊点界面处金属间化合物的形成与长大行为的影响.试验发现,焊点界面处金属间化合物在长时间热循环条件下有明显长大的趋势,并在2000周期后出现了Cu3Sn相,导致焊点力学性能下降,而微量Ce元素能有效抑制界面处以及钎料内部金属间化合物的粗化,从而缓解热循环对焊点力学性能的不利影响.结果表明,随着热循环周期的增加,引脚焊点的拉伸力逐渐降低,添加0.05%Ce元素可有效提高焊点的可靠性. 相似文献
2.
3.
SnAgCu/SnAgCuCe焊点的显微组织与性能 总被引:1,自引:1,他引:1
针对SnAgCu和SnAgCuCe两种无铅焊点,研究焊点内部组织、力学性能及热疲劳特性。研究结果表明,稀土元素Ce的加入可以提高焊点的力学性能,稀土元素的添加可以使SnAgCu焊点拉伸力提高近12.7%。稀土元素的添加细化SnAgCu基体组织,同时减小金属间化合物颗粒(Cu6Sn5和Ag3Sn)的尺寸,这是SnAgCuCe焊点力学性能提高的主要原因。拉伸断裂后的扫描电镜分析表明,两种焊点的断裂呈现明显的韧性断裂特征。另外在温度循环载荷下,稀土元素可以显著提高SnAgCu焊点的疲劳寿命。基于有限元模拟发现SnAgCuCe的抗蠕变性能显著高于SnAgCu焊点。 相似文献
4.
5.
Melting temperature,spreadability,mechanical properties and the microstructures of joints brazed with silver-base filler metals including different amounts of Ga and/or In were studied respectively in this paper,and the results show that the melting temperature of the silver-base filler metals is decreased,spreadability of the silver-base filler metals is improved,and the microstructures of silver-base filler metals are refined obviously with the addition of Ga and/or In.Using copper and brass plates as base metal and brazing with flame method,the mechanical properties of the lap-joint and butt joint were also examined and analyzed respectively,and the results indicate that the fracture position of two kinds of brazed joints occurred on the base metal,except for the lap-joint of brass,which shows better mechanical properties of the joints brazed with the silver-based filler metals including Ga.For the lap-joint of brass,the tensile strength gradually increased with the increase of Ga content,while the addition of In has little effect on mechanical properties.It is also found that the best comprehensive properties of cadmium-free Ag-Cu-Zn filler metals are obtained when Ga content is about 3.0 wt.% and In content is between 1.5 wt.% and 2.0 wt.%. 相似文献
6.
研究了不同镓含量银钎料的熔化温度、铺展性能、钎缝力学性能以及钎料的显微组织变化规律.结果表明,随银钎料中Ga元素含量的增加,钎料的熔化温度降低,铺展性能改善,且显微组织有明显改变.分别以紫铜、黄铜为母材,采用火焰钎焊方法,采用对接和搭接接头形式进行钎焊,研究了钎焊接头的力学性能.除黄铜对接外,其它形式的接头断裂位置均在母材上,说明含镓银钎料的力学性能优良;对于黄铜对接接头来说,钎焊接头的抗拉强度随银钎料中镓含量的增加而逐渐增大,当镓含量为3%时,钎料的综合性能最好. 相似文献
7.
研究了微量稀土元素Pr对Ag30CuZnSn钎料的熔化温度、润湿性能、钎缝力学性能以及钎料显微组织的影响规律.结果表明,随着镨含量的增加,钎料的润湿性有所改善,但当镨含量超过0.15%(质量分数,下同)时,钎料的润湿性反而会变差;钎缝力学性能试验结果显示,随着Pr元素的加入,钎缝抗拉强度增加,当镨含量达到0.15%时抗拉强度达到最大值;钎料显微组织分析表明,镨的加入能够细化Ag30CuZnSn钎料的晶粒,镨的添加量达到0.15%时钎料显微组织最佳,与钎料润湿性能、钎缝力学性能的变化规律吻合. 相似文献
8.
9.