顶部籽晶法生长磁光晶体硼酸铁

本文首次采用顶部籽晶泡生法在敞开体系中生长了出了磁光晶体硼酸铁单晶。选用Ｂ２Ｏ３作自助溶剂，ＬｉＦ作稀释剂，确定了原料配方。对长出的晶体作了初步的物化性能测试。讨论了晶体生长的结果。     

Effects of Post-Thermal Treatment on Quality of SiC Grown by PVT Method

We report the effects of post-thermal treatment on the quality of 2-inch 6H-SiC wafer cut from a crystal boule grown by physical vapour transportation method. The full widths at half maximum of x-ray diffraction rocking curves measured on sites across the 2-inch wafer become narrower, indicating the quality improvement after a three-step post-thermal treatment. It is found that the most common defects such as micropipes and inclusions can be significantly reduced after the treatment. Our results show that the post-thermal treatment is an effective route to improve the quality of SiC single crystals.     

物理气相传输法合成AlN单晶性能表征

采用物理气相传输(PVT)法通过同质外延生长获得14 mm×12 mm的AlN单晶样品。对样品进行切割、研磨、化学机械抛光处理后，采用拉曼光谱仪、高分辨X射线衍射仪、X射线光电子能谱仪、光致发光光谱仪对样品进行测试表征。拉曼测试结果表明，晶体中心区域的拉曼光谱E₂(high)声子模的半峰全宽为3.3 cm^-1,边缘区域E₂(high)声子模的半峰全宽为4.3 cm^-1,晶体呈现较高的结晶质量。XRD摇摆曲线表征结果显示，外延生长后的晶体中心和边缘区域的摇摆曲线半峰全宽增大至100″和205″,表明晶体内存在缺陷。XPS测试结果表明，晶体内存在C、O、Si杂质元素，杂质的原子数分数分别为0.74%、1.43%、2.14%,晶体内发现以氧杂质为主的Al—O、N—Al—O等特征峰。光致发光光谱测试结果显示，晶体内存在V_Al-O_N复合缺陷和V_Al点缺陷。     

金属片加热区熔法单晶生长及应用

在比较现有的各种溶体生长方法的基础上,针对氕物晶体生长的特点,提出了适合均匀生长非固液同成份氧化物晶体的金属片加热区溶法,对该方法的装置、优缺点以及国内外研究现状作了详细的介绍,报道并讨论了应用铂片加热区溶法生长化学计量比铌酸锂晶体的试验及结果。     

多孔石墨对碳化硅晶体生长影响的数值模拟研究

SiC是新一代射频器件和功率器件的理想材料，电阻式物理气相传输法由于具有温度均匀性，成为生长大尺寸SiC单晶的有效方法。近年来，多孔石墨等的使用提高了SiC晶体的质量和产量，而关于其机理的研究却相对较少。本文使用数值模拟的方法系统研究了多孔石墨对SiC晶体生长的影响，并进行了晶体生长验证。模拟结果表明：多孔石墨的使用提高了原料区域的温度及温度均匀性，增大了坩埚内轴向温差，对减弱原料表层的重结晶也具有一定作用；在生长腔内，多孔石墨改善了物质流动在整个生长过程中的稳定性，提高了生长区域的C/Si比，有助于减小相变发生概率，同时多孔石墨对晶体界面也起到改善作用。晶体生长结果实际验证了多孔石墨在提高传质均匀性、降低相变发生率和改善晶体外形上的作用。本文结果对于理解多孔石墨的作用机理以及改善SiC晶体生长条件具有实际意义。     

PVT法SiC单晶生长传热分析

研究了PVT法生长SiC过程中的传热行为,以优化生长条件、获得高质量单晶.该研究是针对坩埚盖(籽晶粘附于坩埚盖上)和炉盖之间的传热行为进行的.研究认为,坩埚盖上部石墨毡开孔形状和大小对坩埚盖的径向温度场有很大影响.采用本文简化的模型可以估算坩埚在不同位置下、不同的石墨毡开孔形状和大小时坩埚盖和炉盖之间总的辐射热阻和传热量.对影响坩埚盖和炉盖之间传热的因素进行了讨论.另外,讨论了在生长过程中动态调整坩埚盖散热条件的可行性.