Transparency and toughness characterization of epoxy resins modified with liquid chloroprene rubber

Transparent epoxy resins modified with liquid chloroprene rubber (LCR), containing in a category of rubber-toughened resin were found. Transparency and toughness characterization of the modified epoxy resins were investigated as a function of LCR content. Epoxy resins modified with 0–10 vol % LCR showed complete phase-separation microstructure. However, these modified resins were transparent, because the refractive index of LCR was compatible with that of the epoxy resin matrix at room temperature. On the other hand, it was observed that above 10 vol % LCR, a certain amount of LCR dissolved into the epoxy matrix. In this case, the glass transition temperature decreased with increasing LCR content. It was also found that the critical stress intensity factor, K _c, of the modified epoxy resins exhibited a maximum between 10 and 15 vol % LCR.     

Breakdown characteristics of oil and paper insulation for a very fast transient voltage

This paper describes the dielectric breakdown characteristics of oil and oil‐impregnated paper for very fast transient (VFT) voltages. Blumlein circuits generate VFT voltages of 60 and 300 ns in a pulse width that simulates disconnecting switching surges in gas‐insulated switch gears. We measured the breakdown voltages of needle‐to‐plane, plane‐to‐plane oil gaps and several pieces of paper between plane electrodes for VFT and lightning impulse voltages. The measured data were formulated in V‐t characteristics and Weibull probability distributions. The inclination n of V‐t characteristics of insulating paper is 150, which is less than n = 13.7 of the plane‐to‐plane oil gap in the VFT time range. The shape parameters of Weibull distribution obtained in this study show that the scattering of breakdown voltages of paper is much less than that of oil. © 2002 Wiley Periodicals, Inc. Electr Eng Jpn, 141(4): 16–24, 2002; Published online in Wiley InterScience ( www.interscience.wiley.com ). DOI 10.1002/eej.10043     

Polarity control of GaN epilayers grown on ZnO templates

We report the successful growth of Ga-polar GaN epilayers on O-polar ZnO templates pre-deposited on c-sapphire. Prior to GaN growth, NH₃ is exposed onto the ZnO template. The polarity of the GaN layers is confirmed by etching of the surface and by conversion beam electron diffraction (CBED), while the O-polar ZnO is confirmed by CBED. It is suggested that the NH₃ pre-exposure helps form a Zn₃N₂ layer, which possesses inversion symmetry and inverts the crystal from anion polar to cation polar.     

Structure of microporous polypropylene sheets containing CaCO3 filler

The microporous polypropylene sheets were prepared by biaxially stretching polypropylene sheets containing CaCO₃ filler (particle size, 0.08–3.0 μm), when the CaCO₃ filler content was 59% by weight and the stretching ratio was 2.8 × 1.8. The microstructure of the sheets were investigated in relation to the CaCO₃ particle size by a N₂ gas permeation method. (1) Effective porosity increases with decreasing mean particle size of filler. (2) The tortuosity factor of the pore is in the range of 25–40 and becomes relatively smaller with decreasing mean particle size of filler. (3) The equivalent pore size becomes relatively smaller with decreasing mean particle size of filler.     

Functions and applications of monostable-bistable transition logicelements (MOBILE's) having multiple-input terminals

The MOBILE is a logic gate exploiting the monostable-bistable transition of a circuit that consists of two resonant tunneling transistors connected in series. It has several advantages including multiple inputs and multiple functions. This paper describes the output characteristics of multiple-input MOBILE's and discusses their applications. For a two-input MOBILE, it is demonstrated that both NAND and NOR operations are possible with the appropriate control voltage. This implies the possibility of a variable function logic gate. Furthermore, the threshold logic operations for a weighted sum of input signals are demonstrated for a three-input MOBILE with a weight ratio of 4:2:1. The applications of MOBILE's in parallel processing architectures such as cellular automata and cellular neural networks are discussed based on the above results. Circuit simulations using a simple model of resonant tunneling transistors successfully reproduce the basic characteristics of MOBILE's, and demonstrate the usefulness of MOBILE's in such applications     

Twin-Related Tetragonal Variants in Yttria Partially Stabilized Zirconia

Crystals of yttria partially stabilized zirconia were grown by the arc-image floating-zone technique and studied by transmission electron microscopy. Crystals annealed at 1700°C consist of tetragonal precipitates and a cubic matrix. The platelike domains in a precipitate are twin-related tetragonal variants stacked alternately parallel to the (011) twin plane. The axial relations between the tetragonal precipitate and the cubic matrix are [100]_tetragonal|[100]_cubic, [011]_tetragonal|[011]_cubic.     

Preparation of spherical fine ZnO particles by the spray pyrolysis method using ultrasonic atomization techniques

An ultrasonic atomizer was used in the spray pyrolysis method to prepare fine, spherical and uniform ZnO particles. Almost spherical particles were obtained successfully which had a mean particle size of 0.15 m and had a very narrow particle size distribution. By using alcohol as the solvent, it was found that the particles do not have hollow shell layers which could usually be observed in the spray pyrolysis process by using water as the solvent. The morphology of the ZnO particles was strongly affected by the concentration of the starting solution.     

Formation of monodispersed Ta2O5 powders

The Ta₂O₅ powders synthesized by the hydrolysis of tantalum pentaethoxide, Ta(OC₂H₅)₅ in alcoholic solution were monodispersed fine oxide particles, which were a uniform, spherical shape, non-agglomerate, and had a narrow size distribution. They grew to 1.2m after ageing for 1 h after hydrolysis. Powder X-ray diffraction and differential thermal analysisthermogravimetric analysis showed the particles were amorphous and hydrated. These particles lost the water at 290° C and gave well-crystalline Ta₂O at 740° C. Throughout these thermal processes, the particle morphology was kept almost the same.     

Structural development in cycloolefin copolymers under uniaxial elongational flow

Development of structures in new cycloolefin copolymers (COCs) of ethylene–norbornene (E–NB) and ethylene–tetracyclododecene (E–TD) of different NB/TD compositions were investigated under uniaxial elongational flow. For E–NB copolymer, which has multiblock sequences, a shoulder in WAXD at 0.76 nm was evident besides its amorphous halo, and the relative intensity of the peak increased with increasing comonomer content (NB). The appearance of a new peak for E–TD copolymer, and a relatively higher intense peak for E–NB copolymer at the same position of 0.76 nm, indicated that local ordering of the segments occurred when the COC was subjected to uniaxial flow. A lower comonomer composition of elongated COC, at a constant Hencky strain rate, exhibited two T_g values, whereas a higher composition showed a single T_g. Both local ordering and segmentization occurred in low comonomer content COCs but only local ordering occurred in higher comonomer content COCs. Both the shear viscosity and roll processing experiments exhibited similar phenomena of segregation. A model is proposed to illustrate the structure of COC after uniaxial elongation/deformation. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 91: 3421–3427, 2004     

Effect of Silicon Dioxide on the Thermal Diffusivity of Aluminum Nitride Ceramics

The thermal diffusivity of AlN ceramics was significantly decreased by the addition of SiO₂. The AlN ceramics with 4 wt% SiO₂ could not be densified by pressureless sintering in the temperature range 1400° to 1800°C. The thermal diffusivity of these samples was very low because of their porous structure. The AlN ceramics containing 2, 4, and 8 wt% SiO₂ were densified by hot-pressing and also had low thermal diffusivity. In these samples, the grains of the 27R polytype that resulted from the reaction between AlN and SiO₂ were dispersed, obstructing the conduction of heat. The relation between the amount of 27R polytype and the thermal diffusivity of the AlN ceramics was determined.